The purpose of the current work was to produce conducting electroactive membranes from bacterial cellulose (BC) coated with polypyrrole (PPy) via in situ chemical polymerization of pyrrole at 4 °C using FeCl 3 as oxidant agent. The electrical conductivity, tensile, thermal and electrochemical properties of BC-PPy membranes were investigated. The results revealed that the uniformly coating of PPy nanoparticles on the surface of BC template achieved high electrical conductivity of 3.39 S cm −1 and a specific capacitance of 191.94 F g −1 at 5 mv s −1 scan rate. The high conductivity and specific capacitance of the present BC-PPy membranes opens new potential applications for BC in various fields as biosensors, flexible electronics, or energy storage devices. [ABSTRACT FROM AUTHOR]

In this work, we prepare cellulose nanopapers of high mechanical performance and with the electrical conductivity of a semiconductor. Cellulose nanofibers (CNF) from bleached softwood pulp were coated with polypyrrole (PPy) via in situ chemical polymerization, in presence of iron chloride (III) as oxidant agent. The structure and morphology of nanopapers were studied, as well as their thermal, mechanical and conductive properties. Nanopaper from pure CNF exhibited a very high tensile response (224 MPa tensile strength and 14.5 GPa elastic modulus). The addition of up to maximum 20% of polypyrrole gave CNF/PPy nanopapers of high flexibility and still good mechanical properties (94 MPa strength and 8.8 GPa modulus). The electrical conductivity of the resulting CNF/PPy nanopaper was of 5.2 10 −2 S cm −1 , with a specific capacitance of 7.4 F g −1 . The final materials are strong and conductive nanopapers that can find application as biodegradable flexible thin-film transistor (TFT) or as flexible biosensor. [ABSTRACT FROM AUTHOR]

In the current work, flexible, lightweight, and strong conductive nanopapers based on cellulose nanofibers (CNFs) with poly(3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) and/or polypyrrole (PPy) were prepared by following a mixing and in situ chemical polymerization method. A successful homogeneous coating of PEDOT:PSS on cellulose nanofibers occurred by means hydrogen-bonding interactions between the hydroxyl functionalized CNF and the electronically charged PEDOT:PSS, as shown by FTIR spectra. The electrical conductivity and the specific capacitance of CNF-PEDOT:PSS nanopapers were 2.58 S cm −1 and 6.21 F g −1 , respectively. Further coating of PPy produced a substantial improvement on the electrical conductivity (10.55 S cm −1 ) and the specific capacitance (315.5 F g −1 ) of the resulting CNF-PEDOT:PSS-PPy nanopaper. A synergistic phenomenon between both conductive polymers supported the high electrical conductivity and specific capacitance of the ternary formulation. Moreover, CNF-PEDOT:PSS-PPy nanopaper showed higher mechanical properties and it was more flexible than the nanopaper containing only polypyrrole conducting polymer (CNF-PPy). It is concluded that the good mechanical, electrical and electrochemical properties of the ternary formulation can apply for smart nanopaper in flexible electronics and energy storage devices. [ABSTRACT FROM AUTHOR]