In this work, a new polymeric binder (polymer of intrinsic microporosity, PIM‐1) has been investigated and discussed to prepare and characterize composite materials for the cathodic oxygen reduction reaction. The new binder is a polymer of intrinsic microporosity, a family of organic compounds with molecularly rigid (glassy) structure, good mechanical and chemical stability. Their influence on the electrocatalytic behaviour of a commercial electrocatalyst during the oxygen reduction reaction in acidic and alkaline media has been investigated, discussed and compared to the behaviour of common cationic and anionic polymer binders, using rotating disk electrode (RDE) techniques. Polymers of intrinsic microporosity perform similarly well, and sometimes better (due to rigidity and gas permeation) when compared to commercial binders. Thus, herein, we showed that PIMs do represent a very promising and versatile alternative as binders in electrocatalysis. [ABSTRACT FROM AUTHOR]

Protonation of the molecularly rigid polymer of intrinsic microporosity PIM-EA-TB can be coupled to immobilisation of Fe(CN)63−/4− (as well as immobilisation of Prussian blue) into 1–2 nm diameter channels. The resulting films provide redox-active coatings on glassy carbon electrodes. Uptake, transport, and retention of Fe(CN)63−/4− in the microporous polymer are strongly pH dependent requiring protonation of the PIM-EA-TB (pKA ≈ 4). Both Fe(CN)64− and Fe(CN)63− can be immobilised, but Fe(CN)64− appears to bind tighter to the polymer backbone presumably via bridging protons. Loss of Fe(CN)63−/4− by leaching into the aqueous solution phase becomes significant only at pH > 9 and is likely to be associated with hydroxide anions directly entering the microporous structure to combine with protons. This and the interaction of Fe(CN)63−/4− and protons within the molecularly rigid PIM-EA-TB host are suggested to be responsible for retention and relatively slow leaching processes. Electrocatalysis with immobilised Fe(CN)63−/4− is demonstrated for the oxidation of ascorbic acid. [ABSTRACT FROM AUTHOR]

Hybrid electrodes with improved O2 tolerance and capability of CO2 conversion into liquid products in the presence of O2 are presented. Aniline molecules are introduced into the pore structure of a polymer of intrinsic microporosity to expand its gas separation functionality beyond pure physical sieving. The chemical interaction between the acidic CO2 molecule and the basic amino group of aniline renders enhanced CO2 separation from O2. Loaded with a cobalt phthalocyanine‐based cathode catalyst, the hybrid electrode achieves a CO Faradaic efficiency of 71 % with 10 % O2 in the CO2 feed gas. The electrode can still produce CO at an O2/CO2 ratio as high as 9:1. Switching to a Sn‐based catalyst, for the first time O2‐tolerant CO2 electroreduction to liquid products is realized, generating formate with nearly 100 % selectivity and a current density of 56.7 mA cm−2 in the presence of 5 % O2. [ABSTRACT FROM AUTHOR]

A film of the polymer of intrinsic microporosity PIM‐7 is coated onto a glassy carbon electrode and the resulting effects on electron transfer reactions are studied for three different types of processes: (i) aqueous solution based, (ii) solid state surface immobilised, and (iii) electrocatalytic processes on electrodeposited palladium. The effects on reactivity for hydroquinone oxidation in aqueous phosphate buffer are shown to be linked to microporosity causing a slightly lower rate of mass transport without detrimental effects on electron transfer and reaction kinetics. Next, water‐insoluble microcrystalline anthraquinone is immobilised directly into the PIM‐7 film and shown to give a chemically reversible reduction process, which is enhanced in the presence of PIM‐7, when compared to the case of anthraquinone immobilised directly onto bare glassy carbon. Electrodeposition of a film of nano‐palladium is demonstrated to give catalytically active electrodes for the reduction/oxidation of protons/hydrogen, the reduction of oxygen, and for the oxidation of formic acid and methanol. With the PIM‐7 film applied onto palladium, a mechanical stabilisation effect occurs. In addition, both the hydrogen insertion and the hydrogen evolution reactions as well as formic acid oxidation are enhanced. Effects are discussed in terms of PIM‐7 beneficially affecting the interfacial reaction under triphasic conditions. The microporous polymer acts as an interfacial "gas management" layer. [ABSTRACT FROM AUTHOR]

Hydrogen oxidation and oxygen reduction are two crucial energy conversion reactions, which are shown to be both strongly affected by the presence of intrinsically microporous polymer coatings on electrodes. Polymers of intrinsic microporosity (PIMs) are known to possess extremely high internal surface area and ability to bind gases under dry conditions. It is shown here that both, hydrogen‐ and oxygen gas binding into PIMs, also occurs under wet or "triphasic" conditions in aqueous electrolyte environments (when immersed in 0.01 M phosphate buffer at pH 7). For two known PIM materials (PIM‐1 and PIM‐PY), nanoparticles are formed by an anti‐solvent precipitation protocol and then cast as a film onto platinum or glassy carbon electrodes. Voltammetry experiments reveal evidence for hydrogen and oxygen binding. Both, PIM‐1 and PIM‐PY, locally store hydrogen or oxygen gas at the electrode surface and thereby significantly affect electrocatalytic reactivity. The onset of oxygen reduction on glassy carbon is shifted by 0.15 V in the positive direction. One for three: Due to their hydrophobic and molecularly rigid nature, intrinsically microporous polymers affect the conditions for gas|liquid electrolyte|solid electrode triphasic reactions. [ABSTRACT FROM AUTHOR]

The enzymeless glucose oxidation process readily occurs on nano-gold electrocatalyst at pH 7, but it is highly susceptible to poisoning (competitive binding), for example from protein or chloride. Is it shown here that gold nanoparticle catalyst can be protected against poisoning by a polymer of intrinsic microporosity (PIM-EA-TB with BET surface area 1027 m2 g−1). This PIM material when protonated, achieves a triple catalyst protection effect by (i) size selective repulsion of larger protein molecules (albumins) and (ii) membrane ion selection effects, and (iii) membrane ion activity effects. PIM materials allow 'environmental control' to be introduced in electrocatalytic processes. [ABSTRACT FROM AUTHOR]

Triphasic microporous materials (containing solid, liquid, and gas) are of interest in electrocatalysis. In this exploratory study, a polymer of intrinsic microporosity (PIM-EA-TB) is impregnated with PdCl 4 2 − metal precursor and vacuum‑carbonised to give an electrically conductive microporous heterocarbon with embedded Pd nanoparticles of typically 10–30 nm diameter. This microporous composite catalyst is formed (via spin-coating) as “flakes” of typically 100 nm thickness and 1 to 20 μm diameter that are readily re-deposited onto glassy carbon electrode substrates. Due to the triphasic conditions, Pd@cPIM electrocatalytic reactivity is high but only for gases (H 2 oxidation or O 2 reduction). This selectivity is observed even in the presence of excess formic acid fuel in the aqueous/liquid phase. The potential for application in membrane-less micro-fuel cells is discussed. [ABSTRACT FROM AUTHOR]

The limited stability of fuel cell cathode catalysts causes a significant loss of operational cell voltage with commercial Pt-based catalysts, which hinders the wider commercialization of fuel cell technologies. We demonstrate beneficial effects of a highly rigid and porous polymer of intrinsic microporosity (PIM-EA-TB with BET surface area 1027 m 2 g − 1 ) in accelerated catalyst corrosion experiments. Porous films of PIM-EA-TB offer an effective protective matrix for the prevention of Pt/C catalyst corrosion without impeding flux of reagents. The results of electrochemical cycling tests show that the PIM-EA-TB protected Pt/C (denoted here as PIM@Pt/C) exhibit a significantly enhanced durability as compared to a conventional Pt/C catalyst. [ABSTRACT FROM AUTHOR]

The enzymeless and operationally simple electrocatalytic oxidation of carbohydrates by “heterogenised” 4-benzoyloxy-TEMPO either (i) immobilised as microcrystals at a glassy carbon electrode surface or (ii) embedded into a polymer of intrinsic microporosity (PIM-EA-TB with 1027 m 2 g −1 BET surface area and highly rigid framework structure) has been studied in aqueous phosphate buffer of pH 12. It is shown that in contrast to microcrystal deposits, 4-benzolyoxy-TEMPO co-immobilised within PIM-EA-TB give stable catalytic responses for both, stationary and rotating disc electrode systems and for oxidation of glucose, sorbitol, and sucrose. The rigidity and intrinsic microporosity of PIM-EA-TB allow (slow) substrate and product diffusion, whilst maintaining 4-benzoyloxy-TEMPO immobilised in active molecular form. [ABSTRACT FROM AUTHOR]

A water-insoluble Polymer with Intrinsic Microporosity (or PIM, here for the particular case of the Tröger Base system PIM-EA-TB, BET area ca. 10 3 m 2 g - 1 ) is demonstrated to act as a rigid host environment for highly water-insoluble molecular catalysts, here tetraphenylporphyrinato-iron (FeTPP), surrounded by aqueous solution-filled micropores. A PIM-EA-TB film containing catalyst is deposited onto the electrode and immersed for voltammetry (i) with 4-(3-phenyl-propyl)-pyridine to give an organogel, or (ii) bare directly into aqueous solution. The porous host allows processes to be optimised as a function of solution phase, composition, and catalyst loading. Effective electron transfer as well as effective electrocatalysis is reported for aqueous oxygen and peroxide reduction. Given the use of completely water-insoluble catalyst systems, the methodology offers potential for application with a wide range of hitherto unexplored molecular electrocatalysts and catalyst combinations in aqueous media. [ABSTRACT FROM AUTHOR]

Highlights: [•] Intrinsically microporous polymers are introduced as electrode modifier. [•] Binding of indigo carmine and PdCl4 − are demonstrated. [•] Formation of Pd metal and catalysis are demonstrated. [ABSTRACT FROM AUTHOR]