Abstract: CaSi2O2N2 phosphors co-doped with Ce3+ and Eu2+ was synthesized via solid-state reaction method. The experiments aimed at optimizing the composition of those phosphors for achieving the highest luminescence intensity as well as at shedding light in the mechanism that governs their luminescence behavior. The overlap of the blue emission spectrum due to Ce3+ with the yellow excitation spectrum due to Eu2+ suggests resonance-type energy transfer mechanism from Ce3+ to Eu2+ taking place in the CaSi2O2N2 host lattice, where electric dipole–dipole interactions dominate. The properties of the produced phosphors qualify them for further consideration in the technology of white light-emitting diodes. [ABSTRACT FROM AUTHOR]

Abstract: Eu2+ and Mn2+ co-doped SrSi2O2N2 green-phosphors, with promising luminescent properties (examined by their powder diffuse reflection, photoluminescence excitation and emission spectra) suitable for UV converted white LEDs, were produced by high temperature solid-state reaction method. The produced materials exhibited intense broad absorption bands at 220–500nm and a broad emission band centered at ca. 530nm, attributed to 4f–5d transitions of Eu2+. The emission intensity of Eu2+ ions was greatly enhanced by introducing Mn2+ ions into SrSi2O2N2:Eu2+ due to the energy transfer from Mn2+ to Eu2+. The energy transfer probability from Mn2+ to Eu2+ depends strongly on the Mn2+ concentration, which is maximized at a Mn2+ concentration of 3mol%. It drastically decreases for higher concentrations. The results indicated that SrSi2O2N2:Eu2+, Mn2+ is a promising green-emitting phosphor for white-light emitting diodes with near-UV LED chips. [Copyright &y& Elsevier]

Abstract: Tb-doped SrSi2O2N2 phosphors with promising luminescent properties were synthesized by the conventional solid-state reaction method, characterized by powder X-ray diffraction and studied by photoluminescence excitation and emission spectra. The synthesized materials exhibited a weak blue emission and a strong green emission in the region of 400–470nm and 480–650nm, which are attributed to 5D3→7F j (j=5, 4, 3) and 5D4→7Fj (j=6, 5, 4, 3) transitions of Tb3+, respectively. The green emission from 5D4→7F5 at 543nm showed the highest intensity under the optimized concentration of 0.1mol, after which the quenching concentration became relevant. The quenching behavior of the emission of Tb3+ was explained by the cross-relaxation of its excited state. [Copyright &y& Elsevier]