Search

The formation and rheological properties of hydrogels based on amphiphilic ABA triblock polyether copolymers are described, relying solely on the hydrophobic interaction of long-chain alkyl glycidyl ether (AlkGE)- based A-blocks that are combined with a hydrophilic poly(ethylene glycol) (PEG) midblock. Via anionic ring-opening copolymerization (AROP), ethylene oxide (EO) and long-chain alkyl glycidyl ethers (AlkGEs) were copolymerized, using deprotonated poly(ethylene glycol) (PEG) macroinitiators ( M n of 10, 20 kg mol -1 ). The polymerization afforded amphiphilic ABA triblock copolymers with molar masses in the range of 21-32 kg mol -1 and dispersities ( Đ ) of Đ = 1.07-1.17. Kinetic studies revealed random copolymerization of EO and AlkGE, indicating random spacing of the hydrophobic AlkGE units by polar EO units. Following this approach, the hydrophobicity of the apolar blocks of amphiphilic ABA triblock polyethers can be tailored. Detailed rheological measurements confirmed the successful formation of hydrogels at different pH values as a consequence of nonpolar interactions and alkyl chain crystallization. Hydrogel formation was also observed at different ionic strengths (i.e., varied salt concentration), based on the hydrophobic aggregates. This behavior is in contrast to other often-used supramolecular cross-linking strategies, such as Coulomb interactions, complexation, or hydrogen bonding. Micro-differential scanning calorimetry (μ-DSC) measurements of the hydrogels revealed crystalline hydrophobic domains with melting temperatures in the physiological temperature range. In 3-[4,5-dimethylthiazol-2-yl]-2,5-diphenyltetrazoliumbromide (MTT) assays, diblock copolymers possessing structural analogy to the triblock copolymers were studied to assess the general cytotoxicity of amphiphilic polyethers bearing long alkyl chains at the polyether backbone, using splenic immune cells. At intermediate polymer concentrations, no cytotoxic effects were observed. This indicates that long-chain alkyl glycidyl ethers are promising for the introduction of highly hydrophobic as well as crystalline motifs at the polyether backbone in hydrogels for biomedical purposes.

Long‐chain epoxides and specifically alkyl glycidyl ethers represent a class of highly hydrophobic monomers for anionic ring‐opening polymerization (AROP), resulting in apolar aliphatic polyethers. In contrast, poly(ethylene glycol) is known for its high solubility in water. The combination of hydrophobic and hydrophilic monomers in block and statistical copolymerization reactions enables the synthesis of amphiphilic polyethers for a wide range of purposes, utilizing micellar interactions in aqueous solutions, e.g., viscosity enhancement of aqueous solutions, formation of supramolecular hydrogels, or for polymeric surfactants. Controlled polymerization of these highly hydrophobic long‐chain epoxide monomers via different synthesis strategies, AROP, monomer‐activated anionic ring‐opening polymerization, catalytic polymerization, or via postmodification, enables precise control of the hydrophilic/lipophilic balance. This renders amphiphilic polymers highly interesting candidates for specialized applications, e.g., as co‐surfactants in microemulsion systems. Amphiphilic polyethers based on propylene oxide and ethylene oxide, such as poloxamers are already utilized in many established applications due to the high biocompatibility of the polyether backbone. Long alkyl chain epoxides add an interesting perspective to this area and permit structural tailoring. This review gives an overview of the recent developments regarding the synthesis of amphiphilic polyethers bearing long alkyl chains and their applications. [ABSTRACT FROM AUTHOR]