Search

Tricalcium diyttrium trisilicon oxide, Ca(3)Y(2)(SiO(4))(3) doped with Eu(2+) and Eu(3+) belongs to a very limited number of hosts able to accommodate both Eu(3+) and Eu(2+) ions, which might make it useful for white light emitting diodes (WLEDs) based on UV chip technology. In this contribution we present a detailed study of photoluminescence kinetics and high pressure spectroscopy of Eu(3+) and Eu(2+) doped Ca(3)Y(2)(SiO(4))(3). At ambient pressure and room temperature, under excitation with near-UV radiation, a broad emission band from 400 to 550 nm due to the 4f(6)5d(1)→4f(7)((8)S(7/2)) transition in Eu(2+) was observed, as well as several emission peaks in the region between 550 and 710 nm, ascribed to the (5)D(0)→ (7)F(J) (J = 0-4) transitions in Eu(3+). The bluish green luminescence related to Eu(2+) in the Ca(3)Y(2)(SiO(4))(3) exhibits a small red pressure-induced shift reaching -5.2 cm(-1)/kbar. The red shifts of the luminescence lines related to Eu(3+) ion emission vary from 0.15 to -0.54 cm(-1)/kbar. Time-resolved photoluminescence was measured at different temperatures and pressures. Luminescence decay traces were studied for the bluish green emission band of Eu(2+) and for the red emission peak due to the (5)D(0) →  (7)F(2) transition of Eu(3+). Decay times slightly decreased with increasing pressure.

Scintillator materials are widely used in X-ray medical imaging detector applications, coupled with available photoreceptors like radiographic film or photoreceptors suitable for digital imaging like a-Si, charge-coupled devises (CCD), complementary metal-oxide-semiconductors (CMOS) and GaAs). In addition, scintillators can be utilized in non-medical imaging detectors such as industrial detectors for non-destructive testing (NDT) and detectors used for security purposes (i.e. airport luggage control). Image quality and dose burden in the above applications is associated with the amount of optical photons escaping the scintillator as well as the amount of optical photons captured by the photoreceptor. The former is characterized by the scintillator efficiency and the latter by the spectral matching between the emission spectrum of the scintillator and the spectral response of the photoreceptor. Recently, a scintillator material, europium-activated lutetium oxide (LuO:Eu), has shown improved scintillating properties. LuO:Eu samples of compact nanocrystalline non-agglomerated powder were developed in our laboratory using homogeneous precipitation from a water-toluene solution in the presence of polyvinyl alcohol as a surfactant. In order to test their light-emission properties, experimental measurements under the excitation of X-ray spectra with X-ray tube voltages between 50 kVp and 140 kVp were performed. This range of applied voltages is appropriate for X-ray radiology, NDT and security applications. LuO:Eu was evaluated with respect to output yield and spectral compatibility of digital imaging photoreceptors (CCD-based, CMOS-based, amorphous silicon a:Si flat panels, ES20 and GaAs). High light yield and spectral compatibility increase the performance of the medical detector and reduce the dose burden to the personnel involved. In addition a theoretical model was used to determine the values for the LuO:Eu optical photon light propagation parameters. The inverse diffusion length was found to be equal to 33 cm/g. In addition LuO:Eu was found to match well with several photoreceptors capable of digital imaging (i.e. GaAs). [ABSTRACT FROM AUTHOR]

The paper reports on the course of decomposition of hydrated lutetium nitrate and lutetium chloride to Lu2O3 in the eutectic mixture of NaNO2 and KNO2. It was shown that a crystallographically pure phase of the cubic Lu2O3 is formed at temperature as low as 250 °C. IR spectra revealed that the recovered powder contains some OH-contamination, however. The powders are characterized by crystallites sizes in the range of 18–30 nm in average. Emission and excitation spectra of Eu-doped powders show characteristic features for Eu3+ ion in an oxide host, which indicates that the procedure is appropriate for making activated nanoparticulate oxide phosphors. Most profound emission appears around 611 nm and the luminescence from the powder made starting with Lu(NO3)3 was noticeably higher compared to the product obtained from LuCl3. The excitation spectrum of Eu3+ emission at 611 nm contains a band related to the fundamental absorption of the lutetia host lattice, which indicates an existence of the host-to-activator energy transfer. [Copyright &y& Elsevier]

Two series of Lu2O3:Eu nanocrystalline phosphors were prepared using either combustion procedure with urea fuel or the Pechini procedure. The dopant concentration varied in both series from 0.2 to 13% with respect to Lu. Despite full crystallization and very similar microstructure of materials of both series, we found profound variations in their spectroscopic properties. The combustion-made phosphors were much less efficient emitters and their emission was strongly concentration-quenched above 3% of the dopant content. For the Pechini-derived materials, the concentration quenching was not observed below 10% of the dopant content and even for the dopant concentrations equal to 10 and 13% the quenching was insignificant. In EPR spectra for Gd3+-doped materials, a significant broadening of lines was found for the combustion-made powders. All these observations imply a strong agglomeration of the dopant ions in the specimens made by applying urea fuel in the combustion process. A semi-two-phase composition was suggested in the combustion-prepared powders. In the Pechini-derived nanocrystalline powders, the dopant ions are uniformly, statistically distributed in the host lattice. [Copyright &y& Elsevier]

Preparation and optical properties of Lu2O3/Eu3+ nanocrystals embedded in silica gel glass are described. The structure of the obtained ceramics was determined by XRD and transmission electron microscopy. It was found that with increasing sintering temperature the Lu2O3/Eu3+ nanocrystallites underwent transformation into monoclinic Lu2Si2O7 nanocrystallites. The fluorescence properties were investigated as a function of thermal treatment of the samples. It was found that after sintering at 1250 °C the fluorescence lifetime increased to 1.5 ms at room temperature. The material studied in this work exhibits a very high intensity of fluorescence with potentials for display application. [Copyright &y& Elsevier]

Review: [discussion of the properties of the broad-band luminescence around 425 nm in the temp. [ABSTRACT FROM AUTHOR]