The occupation sites of Dy- or Y-substituted PZT films were identified using Raman spectroscopy, and the correlation between the occupation site and ferroelectric property was investigated. When Dy or Y was less than 2%, the ferroelectric properties improved because substitution occurred at the B-sites of the PZT films. However, the ferroelectric properties decreased when the substituted ions exceeded 4% because substitution occurred at both B- and A-sites. Consequently, it is important to accurately introduce substituted ions into the B-sites in a PZT film to improve the ferroelectric properties. [ABSTRACT FROM AUTHOR]

Tetragonal Pb(Zr, Ti)O3 films were epitaxially grown on SrRuO3-coated SrTiO3 substrates by metal organic chemical vapor deposition. Perfect polar-axis-oriented 50 nm thick tetragonal films were successfully grown on (100)SrRuO3//(100)SrTiO3 substrates. The single phase of the tetragonal symmetry region was expanded to a Zr/(Zr + Ti) ratio of around 0.6 for these films but was reduced to around 0.4 when (100)/(001)-mixture oriented 250 nm thick films were obtained. The dependence of spontaneous polarization (Ps) on the lattice parameter of c-axis to a-axis (c/a ratio) was demonstrated using perfectly polar-axis-oriented films with various Zr/(Zr + Ti) ratios. The 250 nm thick (100)/(001), (110)/(101), and (111)-oriented tetragonal films were grown on (100), (110), and (111)-oriented substrates. The domain structure was analyzed in detail, and it was found that the observed saturation polarization (Psat) value can be explained by the Ps value and the 90° domain contribution. These data clearly demonstrate the importance of epitaxial film research for actual ferroelectric random access memories applications. [ABSTRACT FROM AUTHOR]

Thin films of Bi(Fe1-xScx)O3 (BFSO) system were fabricated on (111)Pt/TiO2/SiO2/(100)Si substrates by chemical solution deposition to improve the electrical resistivity by substituting electrically unstable Fe3+ cations for stable Sc3+ cations. A single phase of perovskite was obtained in the range of x=0–0.30, in which selective replacement of Fe3+ and Sc3+ was confirmed in x=0–0.15 by using Raman measurement. The leakage current density of the BFSO films was reduced by increasing x. A well-saturated polarization–electric field hysteresis loop was obtained for BFSO films with x=0.15, showing remanent polarization of approximately 35 μC/cm2. [ABSTRACT FROM AUTHOR]