Search

The output of bio-based polyvinyl alcohol (PVA) has been growing rapidly with a substantial increase of developments both in academic and industrial research areas in the past decade, which is due to its water solubility, plasticity, and degradability. However, PVA is highly flammable with a limiting oxygen index of only 19% owning to its inherent macromolecular structure composed of carbon, hydrogen, and oxygen atoms. The demand for flame retardancy of PVA has been increased rapidly and is generally satisfied by introducing flame retardants via chemical grafting, physical blending, and coating. This review summarizes the flame retardants applied in PVA and their influence on the flammability and mechanical properties of PVA materials. The type of flame retardant additives and their application technologies for various PVA products are presented in terms of various PVA products, such as films, aerogel, fibers, foams, and bulk composites. The films dominate the whole research of flame retardant PVA materials owing to their widespread application. The fire performance and flame retardant mechanism are compared and discussed. Additionally, PVA acted as an assistant agent in some polymeric flame-retardant formulations is also discussed and reviewed. [ABSTRACT FROM AUTHOR]

It is still a big challenge for textile industry in improving fire resistance and reducing melt dripping with minimal loss on the physical properties of polyethylene terephthalate (PET) fabrics. In this work, a highly-effective hyperbranched flame retardant (DT) was first synthesized by ester exchange without using any organic solvent. Then, the DT foam was prepared and blade coated on PET fabric to improve the fire performance. The prepared PET fabric with only 2.7% weight gain of DT was self-extinguished and did not produce any molten dripping during the vertical flammable test. The peak heat release rate and total heat release of the PET fabric sample with 19.4% DT were decreased by 42.0% and 57.1%, respectively compared with that of the control PET. Besides, the as-prepared PET fabric sample showed better physical properties such as breaking strength, vapor permeability, air permeability, antistatic property, and softness than the control PET fabric sample. The DT foam finishing process did not involve any organic solvent and consumed less water and energy compared with conventional fabric treatments. It is expected that this work provides a facile and eco-friendly strategy for fabricating flame retardant PET fabric with excellent comprehensive performances. [Display omitted] • A hyperbranched flame retardant (DT) was synthesized by a solvent-free approach. • Flame retardant PET fabrics were prepared by sustainable foam finishing. • The PET fabric with 2.7% DT was self-extinguished and free of molten drops. • The treated PET fabric showed excellent physical properties. [ABSTRACT FROM AUTHOR]

• Phosphorylated histidine-amino triazine-diaminopropane (PHTD) copolymer was synthesized and used as bifunctional additives of flame retardant and binder. • PHTD can improve the flame retardancy and smoke suppression of EPS foams significantly. • The hard shell formed by PHTD can improve the compressive strengths of EPS foams. A novel intumescent flame retardant, phosphorylated histidine-amino triazine-diaminopropane (PHTD) was synthesized and utilized as both a flame retardant and a binder addition. Flame retardant expanded polystyrene (EPS) foams containing PHTD was successfully prepared by coating method. The limited oxygen index (LOI) and vertical burning (UL-94) tests were used to determine the flammability of EPS/PHTD composite foams, and an apparent flame retardant effect could be obtained with up to 28.8% LOI value and UL-94 V-0 rating when 41.9 wt.% PHTD was added. The cone calorimetric test results showed that the treat EPS sample showed significantly depressed peak heat release rate (pHRR) by 74.9% and peak smoke production rate (pSPR) by 77.3%. Additionally, the flame retardant could be evenly coated on the surface of EPS beads. Even though part of the foam was damaged, it could still keep good flame retardant performance. Furthermore, the thermal conductivity of coated foam was not affected and remained at a comparatively low level, and the compressive strength was increased by 20.0%. [ABSTRACT FROM AUTHOR]