TiO2 nanoparticles can improve the electrical performance of oil paper insulation. In this study, 10 nm TiO2 nanoparticles were prepared and dispersed into transformer oil, and then immerse pressboards in it to obtain nanofluid impregnated pressboards (NP). Its thermal aging was accelerated together with the reference sample at 130°C for 36 days. Analyzing the acid value in the oil, polymerization degree, surface topography, AC breakdown strength, surface flashover characteristics and surface potential decay characteristics. It was observed that TiO2 nanoparticles can reduce the acid value and improve AC breakdown strength of oil. However, the degree of polymerization and surface appearance of NP and oil impregnated pressboards (OP) during thermal aging did not differ significantly. During the aging process, the energy level of pressboard surface traps shifted first towards the shallow and then gradually towards the deep. During all the aging stages, the surface flashover voltage of NP was always higher or close to that of OP. The mechanism of TiO2 nanoparticles improving the breakdown and surface flashover characteristics of oil–paper insulation during thermal aging is discussed from the perspective of water molecules and aging by‐products adsorption and introduction of shallow traps by nanoparticles. [ABSTRACT FROM AUTHOR]

With the aim of exploring an alternative method of nano-doping in cellulose paper and improving flashover strength of oil-impregnated paper, radio frequency (RF) magnetron sputtering method is introduced into the structural modification of insulating paper for converter transformers. In this experiment, insulating paper was treated with ZnO sputtering for 0, 7.5, 15 and 30 min, respectively. The surface morphology of dry paper was observed with a scanning electron microscope. The bonding mode of sputtered ZnO particles with cellulose matrix was investigated via attenuated total reflection infrared (ATR-IR) spectroscopy and mechanical property of the sputtered samples were studied. Surface and volume conductivities of the oil-impregnated sputtered paper were measured. Moreover, the charge dissipation characteristics of sputtered insulating paper was investigated by means of surface potential decay. In addition, trap distribution and carrier mobility of specimen were further obtained. Finally, the DC flashover strength were tested. The results showed that ZnO magnetron sputtering had a distinct influence on the structure of the insulating paper, resulting in the formation of hydrogen bond and chemical bond and an increase of the surface and volume conductivities. ZnO sputtering was found to decrease the initial potential and accelerate charge decay. Moreover, appropriate sputtering enhanced the surface flashover strength.