Search

Purpose: To compare the flexural strength and modulus of ball-soft liner–retained overdentures vs ballsocket– retained overdentures, as well as to evaluate the effect of using glass fiber reinforcement on the mechanical properties of ball-soft liner–retained overdentures.Materials and Methods: A total of 80 overdenture specimens were fabricated and divided equally into four groups (n = 20/group): specimens with a metal matrix (group 1); a silicone soft liner matrix (group 2); reinforced with one bundle of unidirectional Stick glass fiber placed above the silicone soft liner matrix (group 3); and reinforced with four weaves of bidirectional Stick Net glass fibers placed above the silicone soft liner matrix (group 4). Half of the specimens from each group were stored in water at room temperature (23°C ± 1°C) for 24 hours, while the other half were stored in water at 37°C for 30 days before being subjected to a static three-point loading test.Results: After 1 day of water storage, the flexural strength and flexural modulus values of groups 1, 3, and 4 were not significantly different from each other (P = .788, P = .084), but were significantly higher than group 2 (P < .05). Water storage for 30 days significantly decreased the flexural strength of group 1 only (P < .001) and not the other three groups (P >.05).Conclusion: Overdentures retained with a metal matrix were not significantly different from those retained with a silicone soft liner matrix in terms of flexural strength and modulus after 30 days of water storage. Placing unidirectional and bidirectional glass-fiber reinforcement above soft liner matrices can increase the flexural strength of ball-soft liner–retained overdentures. [ABSTRACT FROM AUTHOR]

The aim of this study was to evaluate the effect of surface polishing as well as the post-curing atmospheres (air and nitrogen gas) on the physical properties of an occlusal splint material for additive manufacturing. Flexural strength, flexural modulus, Vickers hardness number (VHN), degree of carbon double bond conversion (DC), water sorption (WSP), and water solubility (WSL) were evaluated. Surface polishing significantly affected the evaluated properties. Regardless of the post-curing atmosphere, flexural strength, flexural modulus, VHN, and DC showed significantly higher values for the polished specimens when compared with the unpolished ones, while WSP and WSL were significantly lower for the polished specimens. Unpolished specimens post-cured at nitrogen gas showed significantly higher VHN and DC values. However, the effect of the post-curing at a nitrogen gas atmosphere was non-significant in polished specimens. The current results suggested that surface polishing plays a role in the physical properties of the evaluated occlusal splint material and can enhance all the evaluated properties regardless of the post-curing atmosphere. Meanwhile, the post-curing at a nitrogen gas atmosphere can enhance the VHN and DC but its effect is confined only to the surface layers, which can be removed during surface polishing. [ABSTRACT FROM AUTHOR]

Despite the fact that three-dimensional (3D) printing is frequently used in the manufacturing of occlusal splints, the effects of the 3D printer type and post-curing methods are still unclear. The aim of this study was to investigate the effect of the printer type (digital light processing: DLP; and liquid crystal display: LCD) as well as the post-curing method with two different atmospheric conditions (air and nitrogen gas (N2)) on the mechanical and surface properties of 3D-printed soft-type occlusal splint material. The evaluated properties were flexural strength, flexural modulus, Vickers hardness (VHN), fracture toughness, degree of double bond conversion (DC%), water sorption, water solubility, and 3D microlayer structure. The printer type significantly affected all the evaluated properties. Flexural strength, flexural modulus, and fracture toughness were significantly higher when specimens were printed by a DLP printer, while VHN and DC% were significantly higher, and a smoother surface was noticeably obtained when printed by an LCD printer. The post-curing at an N2 atmosphere significantly enhanced all of the evaluated properties except water sorption, 3D microlayer structure, and fracture toughness. The current results suggested that the printer type and the post-curing methods would have an impact on the mechanical and surface properties of the evaluated material. [ABSTRACT FROM AUTHOR]

Although three-dimensional (3D) printing is clinically convenient to fabricate occlusal splints, it is still unclear how the post-curing method and the printer type can affect 3D-printed splints. This study aimed to evaluate the effect of stroboscopic post-curing at a nitrogen gas (N2) atmosphere versus post-curing in an air atmosphere, as well as the printer type (liquid crystal display (LCD) and digital light processing (DLP)) on the mechanical properties of a 3D-printed hard-type occlusal splint material. Flexural strength, flexural modulus, Vickers hardness number (VHN), fracture toughness, degree of double bond conversion (DC), 3D microlayer structure, water sorption, and water solubility were evaluated. The post-curing method significantly affected all evaluated properties except fracture toughness and 3D microlayer structure, while the printer type significantly affected all evaluated properties except flexural strength and flexural modulus. VHN and DC were significantly higher, and the smoother surface was noticeably obtained when printed by LCD printer and post-cured at an N2 atmosphere. The current results suggested that the post-curing method and the printer type would play a role in the mechanical properties of the evaluated material and that the combination of post-curing at an N2 atmosphere and LCD printer could enhance its mechanical properties and surface smoothness. [ABSTRACT FROM AUTHOR]

This study investigated some mechanical properties of five CAD/CAM materials used for the fabrication of provisional restorations and tooth segments for digitally fabricated dentures. The CAD/CAM blocks were sectioned into bars for flexural strength and elastic modulus testing (n=80), and for surface microhardness (n=80). Half of the specimens were water-stored for 30 days while the other half was dry-stored. Additional specimens were prepared for bond strength (n=40). A 2-way analysis of variance (ANOVA) was conducted to detect the effect of material and water storage (α=0.05). Statistical software (IBM SPSS Statistics v21; IBM) was used for conducting all analyses. Material type and storage significantly affected the flexural strength, flexural modulus and microhardness (p<0.001). The type of material did not have a significant effect on bond strength (p>0.05). The tested materials showed variation in their flexural properties and surface microhardness whereas their bonding properties with resin luting cement were similar. [ABSTRACT FROM AUTHOR]

To evaluate the effect of post-curing method, printing layer thickness, and water storage on the mechanical properties and degree of conversion of a light-curing methacrylate based resin material (IMPRIMO® LC Splint), used for the fabrication of 3D printed occlusal splints and surgical guides. 96 bar-shaped specimens were 3D printed (Asiga MAX), half of them with a layer thickness of 100 μm (Group A), and half with 50 μm (Group B). Each group was divided in three subgroups based on the post-curing method used: post-curing with light emitting diode (LED) and nitrogen gas; post-curing with only LED; and non-post-curing. Half of the specimens from each subgroup were water-stored for 30 days while the other half was dry-stored (n = 8). Flexural strength and flexural modulus were evaluated. Additional specimens were prepared and divided in the same way for surface hardness (n = 96), fracture toughness, and work of fracture (n = 96). Five specimens were selected from each subgroup for evaluating the degree of conversion (DC). Data were collected and statistically analyzed with 1-way, 2-way ANOVA, and Tukey post-hoc analysis (α = 0.05). The 2-way ANOVA showed that the post-curing method and water storage significantly affected the investigated mechanical properties (P < 0.001). The 1-way ANOVA revealed a statistically significant difference among the tested groups on the investigated properties (P < 0.001). After water storage, the 100 μm subgroup post-cured with only LED showed higher flexural strength (51 ± 9) than the 50 μm and 100 μm subgroups that were post-cured with LED in addition to nitrogen gas atmosphere (38 ± 5, 30 ± 3) (p < 0.05). The 50 μm subgroup post-cured with only LED showed the highest significant flexural modulus values (1.7 ± 0.08) (p < 0.05). However, the 50 μm subgroup post-cured with LED plus nitrogen showed significantly higher surface hardness values (p < 0.05) among the investigated groups. The non-post-cured subgroups showed the lowest values, which were significantly different from the other subgroups (p < 0.05). The post-curing method, water storage, and printing layer thickness play a role in the mechanical properties of the investigated 3D Printed occlusal splints material. The combination of heat and light within the post-curing unit can enhance the mechanical properties and degree of conversion of 3D printed occlusal splints. Flexural strength and surface hardness can increase when decreasing printing layer thickness. [ABSTRACT FROM AUTHOR]