Aluminum and A356 alloy foam castings are produced using a melt-foaming method. Prior to foaming, the melt is modified with nano-sized particles (SiC, TiN, or Al2O3). The nano-sized particles are mixed with micro-sized Al particles, which are ultrasonically treated and hot-extruded. Thus, the so-called "modifying nano-composition" is obtained. The resulting compositions are introduced into the melt of the Al foam at the following mass concentrations of nanoparticles: SiC: 0.038 wt. %; TiN: 0.045 wt. %; and Al2O3: 0.046 wt. %. For the A356 foam, we use the following concentrations: SiC: 0.039 wt. %; TiN: 0.052 wt. %; and Al2O3: 0.086 wt. %. The macrostructure of the foam castings is investigated by CT scanning and 3D analysis. The pore size distributions and accumulative fraction dependencies are determined for all samples. The microstructure of the foam castings is investigated by SEM-EDS analysis. The results confirmed the presence of individual nano-sized particles, as well as clusters of particles in foam walls. The conducted compression tests show a significant increase in the plateau stress (up to 237%) of the modified aluminum foam castings compared to non-modified castings. However, a similar effect of the nano-compositions on A356 alloy foam castings is not observed. The obtained results show that the above-indicated concentrations of nanoparticles can positively influence the mechanical properties of aluminum foam castings. The novelty of the current study is two-fold: (1) such low concentrations of added nanoparticles have never been used before to alter Al foam's properties, and (2) an original method of introducing the nanoparticles into the melt is applied in the form of nano-compositions. [ABSTRACT FROM AUTHOR]

Cylindrical foam castings of Al and A356 alloy were produced using a melt foaming method with the introduction of Ca and TiH2. Foam crystallization takes place in a cooled thin-walled metal mold. Samples cut off from the foam castings are investigated by X-ray tomography, quantitative data for porosity, average pores diameter and average cells wall thickness are obtained. It is found that the porosity is mainly open. Same samples are tested in quasi-static mode and the compressive strength is determined. The influence of porosity on compressive strength is analyzed. [ABSTRACT FROM AUTHOR]

A method for determining the thermal conductivity coefficient of a foam material of A356 aluminum alloy has been proposed. The foam material has been produced by decomposition of titanium hydride introduced into the melt and subsequent cooling and crystallization. During the process, the measurement of temperature dependences on time has been performed at two selected points of the foam casting. The problem of heat transfer and crystallization of the casting and mold is solved by means of mathematical model proposed. The experimental data and the corresponding solutions of the mathematical model have been used for the realization of an identification procedure for determining the coefficient of thermal conductivity of the foam material and the coefficient of heat transfer at the casting-mold boundary. Through the represented methodology new data for important thermophysical characteristic are obtained. [ABSTRACT FROM AUTHOR]