Search

This work deals with the durability of a Pinus elliotti wood impregnated with alumina (Al2O3) particles. The samples were impregnated at three different Al2O3 weight fractions (c.a. 0.1%, 0.3% and 0.5%) and were then exposed to two wood-rot fungi, namely white-rot fungus (Trametes versicolor) and brown-rot fungus (Gloeophyllum trabeum). Thermal and chemical characteristics were evaluated by Fourier transform infrared spectroscopy (FT-IR) and thermogravimetric (TG) analyses. The wood which incorporated 0.3 wt% of Al2O3 presented a weight loss 91.5% smaller than the untreated wood after being exposed to the white-rot fungus. On the other hand, the highest effectiveness against the brown-rot fungus was reached by the wood treated with 5 wt% of Al2O3, which presented a mass loss 91.6% smaller than that of the untreated pine wood. The Al2O3-treated woods presented higher antifungal resistances than the untreated ones in a way that: the higher the Al2O3 content, the higher the thermal stability. In general, the impregnation of the Al2O3 particles seems to be a promising treatment for wood protection against both studied wood-rot fungi. Additionally, both FT-IR and TG results were valuable tools to ascertain chemical changes ascribed to fungal decay. [ABSTRACT FROM AUTHOR]

This study aimed to evaluate the variations in thermal and chemical characteristics of juvenile Eucalyptus grandis wood submitted to a deterioration test by Nasutitermes termites. For this purpose, a biodeterioration test with termites was conducted according to ASTM D 3345 (2008), in which, after the end of the period corresponding to the test (40 days), we evaluated the mass loss, chemical composition and thermal stability of the main components of the deteriorated wood samples and those belonging to the control group. We found that deterioration due to exposure of the samples to Nasutitermes sp. termites caused a mass loss of 66,88% for wood with a density at 12% moisture content of 412 kg/m³. The quantitative chemical composition showed a reduction in the contents of cellulose, hemicellulose and lignin. Analysis of the variations of the organic functional groups related to the chemical composition of the wood by Fourier Transform Infrared Spectroscopy and relative intensity of the spectral bands also showed reductions, demonstrating homogeneous deterioration of the main components of the deteriorated woods. The thermal stability showed an increase in deteriorated wood for most of the temperature ranges, mainly for those that corresponded to losses in moisture and volatiles (25 °C - 100 °C), hemicelluloses (240 °C - 300 °C), celluloses, and together with initial lignin degradation (310 °C to 400 °C), possibly due to the removal of cellulose and hemicellulose, as well as the deposition of substances expelled by the termites in the cell wall. From the results, we conclude that the termites do not have specificity regarding the chemical component and that the deterioration caused variations in the chemical composition of the wood, whereas the opposite was observed for thermal stability, which presented an increase in most of the temperatures ranges for the deteriorated woods compared to the control group. [ABSTRACT FROM AUTHOR]

This study aimed to analyze chemical changes by Fourier Transform Infrared Spectroscopy of Eucalyptus dunnii and Pinus elliottii treated woods subjected to an accelerated decay test with the white rot fungus Ganoderma applanatum. The wood test specimens (2,5x2,5x0,9 cm) were impregnated with preservative solutions of chromated copper borate and synthetic pyrethroids and carbamates with 6% concentration by a vaccum-pressure process. After a decay test of 16 weeks, the chemical changes of the treated and untreated wood samples were evaluated by Fourier Transform Infrared Spectroscopy. It was observed that the rot fungus attack caused a variation in the intensity and a displacement of spectrum peaks, indicating a change to the woods' chemical composition after fungal exposure. The lignin / carbohydrate ratio indicated that the fungus had no preference for a specific cell wall component, pointing to a simultaneous deterioration of cellulose, hemicellulose and lignin in the treated and untreated woods. Finally, the Fourier Transform Infrared Spectroscopy technique, together with the lignin / carbohydrate ratio analysis, proved efficient in the study of the variation of the wood chemical modifications deteriorated by rot fungi. [ABSTRACT FROM AUTHOR]