Search

Multiwalled carbon nanotubes (MWCNTs) were used as nanotemplates for the dispersion and stabilization of FePt nanoparticles (NPs). Pre-formed capped FePt NPs were connected to the MWCNTs external surface via covalent binding through organic linkers. Free FePt NPs and MWCNTs-FePt hybrids were annealed in vacuum at 700 °C in order to achieve the L10 ordering of the FePt phase. Both as prepared and annealed samples were characterized and studied using a combination of experimental techniques, such as Raman and Mössbauer spectroscopies, powder X-ray Diffraction (XRD), magnetization and transmittion electron microscopy (TEM) measurements. TEM measurements of the hybrid sample before annealing show that a fine dispersion of NPs along the MWCNTs surface is achieved, while a certain amount of free particles attached to each other in well connected dense assemblies of periodical or non-periodical particle arrangements is also observed. XRD measurements reveal that the FePt phase has the face-centered cubic (fcc) disordered crystal structure in the as prepared samples, which is transformed to the face-centered tetragonal (fct) L10 ordered crystal structure after annealing. An increase in the average particle size is observed after annealing, which is higher for the free NPs sample. Superparamagnetic phenomena due to the small FePt particle size are observed in the Mössbauer spectra of the as prepared samples. Mössbauer and magnetization measurements of the MWCNTs-FePt hybrids sample reveal that the part of the FePt particles attached to the MWCNTs surface shows superparamagnetic phenomena at RT even after the annealing process. The hard magnetic L10 phase characteristics are evident in the magnetization measurements of both samples after annealing, with the coercivity of the hybrid sample over-scaling that of the free NPs sample by a factor of 1.25.

We use ultraviolet photoelectron spectroscopy to investigate the effect of oxygen and air exposure on the electronic structure of pentacene single crystals and thin films. it is found that O-2 and water do not react noticeably with pentacene, whereas singlet oxygen/ozone readily oxidize the organic compound. Also, we obtain no evidence for considerable p-type doping of pentacene by O-2 at low pressure. However, oxygen exposure lowers the hole injection barrier at the interface between An and pentacene by 0.25 eV, presumably due to a modification of the An surface properties.

We report a study of acid-terminated self-assembled monolayers of alkanethiols of different length, 11-mercaptoundecanoic acid (11-MUA) and 16-mercaptohexadecanoic acid (16-MHDA), on Au(111). Scanning tunneling microscopy (STM), X-ray photoelectron spectroscopy (XPS), cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and contact angle techniques were used for characterization, and the results were compared with those obtained from n-alkanethiols of similar chain length, providing a detailed description of the two-dimensional crystalline structure. Molecular resolution STM images show that 11-MUA forms a dense-packed monolayer arranged in a (square root 3 x square root 3)R30 degrees structure with a c(2 x 4) superlattice, where the simple hexagonal phase, the c(2 x 4) superlattice, and nonordered areas coexist. 16-MHDA assembles in a uniform monolayer with similar morphology to that of 11-MUA, but molecular resolution could not be reached in STM due to both the hydrophilicity of the acid groups and the poor conductivity of the thick monolayer. Nevertheless, the monolayer thicknesses estimated by XPS and electrochemistry and the highly blocking character of the film observed by electrochemistry as well as the low water contact angle are consistent with 16-MHDA molecules forming a compact monolayer on the Au(111) substrate with fully extended alkyl chains and acid groups pointing away from the surface. The results obtained for 16-MHDA were reproducible under different preparation conditions such as the addition or omission of acetic acid to the ethanolic solution. Contrary to other reports, we demonstrate that ordered acid-terminated self-assembled monolayers are obtained with the same preparation conditions as those of the methyl-terminated ones, without any additional treatment.