CsPbBr3−xIx quantum dots were precipitated in boro‐germanate glasses with various Br/I ratios by the melt‐quenching method. When the heat treatment temperature (TH) increased from 480 to 550°C, more I− entered the perovskite crystal lattice, resulting in lattice expansion, the X‐ray diffraction peaks of CsPbBr1.5I1.5 glasses shifted to small angles. The high concentration of I− entered into the perovskite crystal lattice, decreasing the bandgap. The photoluminescence (PL) peaks of CsPbBr1.5I1.5 glasses redshifted from 577 to 620 nm, the PL peaks of CsPbBrI2 glasses shifted from 614 to 636 nm, and the PL peaks of CsPbBr0.5I2.5 glasses shifted from 650 to 672 nm. As the ratio of Br/I reduced from 2.5/0.5 to 0.5/2.5, the PL lifetime of CsPbBr3−xIx glass increased from 2.08 to 74.5 ns. With the delay time from 1 to 1500 ps, the carriers gradually accumulated in the band‐edge state, and the bleaching signal intensity increased. Then more and more carriers returned to the ground state through radiative or nonradiative recombination, the bleaching signal intensity decreased. [ABSTRACT FROM AUTHOR]

CdS/Cd 1−x Zn x S sandwich-structured quantum dots (QDs) were precipitated in silicate glasses with high quantum efficiency up to 53%. The QDs were composed by a CdS core with a Cd 1−x Zn x S shell of about 1–3 nm in thickness through heat-treatment at 550 °C for 10 h. With the increased heat-treatment temperature, the intensity ratio between the intrinsic emission and the defects emission increased and the Stokes shift decreased from 84 to 4 meV, which was caused by both the increased size and passivated surface defects of the QDs. [ABSTRACT FROM AUTHOR]