Ceramics joining has been widely applied in MEMS sensors, microwave and imaging devices as well as other ceramic packaging applications to fabricate multifunctional ceramic components. In this study, a glass frit with gradient thermal expansion coefficient (TEC) has been applied as the bonding material to join the ceramic of Al 2 O 3 and AlN. This glass frit consists of two types of glasses with different TEC. The Al 2 O 3 and AlN ceramics have been successfully joined with this glass frit in muffle furnace at 850 °C for 1 h. The bonding strength of Al 2 O 3 /AlN ceramic joined via this glass frit exceeds 40 MPa without any cracks in the joining interface, which is much superior compared with that of conventional glass frit bonding. Our work demonstrates that the gradient-TEC glass frit bonding is an effective method to join different types of ceramics. [ABSTRACT FROM AUTHOR]

The influence of BaO content (up to 15 mol%) on the crystallization behaviour, structure, thermal properties and microwave dielectric properties of the BaO-CaO-B 2 O 3 -SiO 2 glasses and glass-ceramics system was investigated. The glasses were produced by melting at 1400 °C and quenching into water, and the glass-ceramics were produced via heat treatment at temperatures between 750 and 800 °C. The results of X-ray diffraction analysis showed that increasing the BaO content raised the resistance of the glass against crystallization and favoured the transformation of β-CaSiO 3 and α-CaSiO 3 phases, which crystallized in the Ba-free and in low BaO content compositions, into SiO 2 and Ba 4 Si 6 O 16 , which crystallized in compositions with higher concentrations of BaO. The BaO content had little influence on the glass transition temperature ( T g ) and the linear coefficient of thermal expansion (CTE), but strongly reduced the softening point ( T s ). Even the addition of BaO as minor additives resulted in a dramatic reduction of the T s ; for example, the T s decreased from 902 °C for the Ba-free composition to 682 °C for the BaO-containing one (5%). Low values of the dielectric constant (5.9 ≤  ε r ≤ 6.63) and dielectric loss (1.12 × 10 −3 ≤ tan δ  ≤ 3.15 × 10 −3 ) were measured. [ABSTRACT FROM AUTHOR]

In this paper, an insulating film was successfully prepared by sintering 35 wt % CaO-15 wt % Al2O3-10 wt % B2O3-40 wt % SiO2 glass at 875 °C. After sintering, the main component of the insulating film was glass-ceramics. The main crystal phase was CaAl2Si2O8, and the crystallization activation energy was 189.76 kJ/mol. After preparing the insulating film, its color turned yellow, and the diffusion of Ag was found by XPS and XRD data. When the temperature increased to 875 °C, the color of the insulating film became lighter, and the silver content decreased. The adhesion of the multilayer structure could reach 875 N. The dielectric constant of the insulating film in the multilayer structure was approximately 5, and the dielectric loss was 0.0011. After sintering, the dielectric strength of the insulating film could reach 13.11 kV/mm, which fully meets the requirements of a complex packaging structure. [ABSTRACT FROM AUTHOR]