In this paper, an insulating film was successfully prepared by sintering 35 wt % CaO-15 wt % Al2O3-10 wt % B2O3-40 wt % SiO2 glass at 875 °C. After sintering, the main component of the insulating film was glass-ceramics. The main crystal phase was CaAl2Si2O8, and the crystallization activation energy was 189.76 kJ/mol. After preparing the insulating film, its color turned yellow, and the diffusion of Ag was found by XPS and XRD data. When the temperature increased to 875 °C, the color of the insulating film became lighter, and the silver content decreased. The adhesion of the multilayer structure could reach 875 N. The dielectric constant of the insulating film in the multilayer structure was approximately 5, and the dielectric loss was 0.0011. After sintering, the dielectric strength of the insulating film could reach 13.11 kV/mm, which fully meets the requirements of a complex packaging structure. [ABSTRACT FROM AUTHOR]

The internal friction (IF) behaviors of a series of LaCe-, Zr-, and La-based bulk metallic glasses (BMGs) were studied by a computer-controlled, conventional inverted torsion pendulum. The results indicate that with an increasing temperature, the IF also increases gradually in the supercooled liquid region, followed by a decrease caused by crystallization. BMGs with a good glass forming ability (GFA) usually possess a high IF peak value for an alloy system with the same constituent elements. Furthermore, the magnitude of the IF value (Qi−1) of the inflection point is an efficient criterion of GFA. The Qi−1 value is a valid criterion under the conditions of identical constituent elements and different element contents. However, Qi−1 and GFA have no relationship among different alloy systems. [ABSTRACT FROM AUTHOR]

Ceramics joining has been widely applied in MEMS sensors, microwave and imaging devices as well as other ceramic packaging applications to fabricate multifunctional ceramic components. In this study, a glass frit with gradient thermal expansion coefficient (TEC) has been applied as the bonding material to join the ceramic of Al 2 O 3 and AlN. This glass frit consists of two types of glasses with different TEC. The Al 2 O 3 and AlN ceramics have been successfully joined with this glass frit in muffle furnace at 850 °C for 1 h. The bonding strength of Al 2 O 3 /AlN ceramic joined via this glass frit exceeds 40 MPa without any cracks in the joining interface, which is much superior compared with that of conventional glass frit bonding. Our work demonstrates that the gradient-TEC glass frit bonding is an effective method to join different types of ceramics. [ABSTRACT FROM AUTHOR]