Search

In the construction industry, the selection of sustainable materials leads to a movement towards more sustainable construction. In this study, lightweight aggregate shotcrete based on expanded glass (EG) and expanded clay (EC) is investigated. The goal of the study is to determine the influence of EG and EC inclusion on the properties of shotcrete. Ordinary Portland cement (OPC) powder with supplementary cementitious materials, such as silica fume and ground glass waste, are used as binders. The mechanical, physical and morphological properties, as well as the mineral and oxygen compositions, are obtained through compressive and flexural strength tests, thermal conductivity measurements, scanning electron microscopy with energy dispersive X-ray spectrometry (SEM–EDX), X-ray diffraction (XRD) and X-ray fluorescence (XRF) analysis. In this study, the mechanical, physical and thermal properties and waste utilization as cement supplementary materials are balanced. The shotcrete samples show that a density of 790 kg/m3 had a good thermal performance (thermal conductivity coefficient of 0.174 W/(m·K)) with the sufficient compressive strength of 6.26 MPa. [ABSTRACT FROM AUTHOR]

This paper analyzes concrete fine aggregate (sand) modification by scrap tire rubber particles-fine crumb rubber (FCR) and coarse crumb rubber (CCR) of fraction 0/1 mm. Such rubberized concrete to get better bonding properties were modified by car-boxylated styrene butadiene rubber (SBR) latex and to gain the strength were modified by glass waste. The following tests—slump test, fresh concrete density, fresh concrete air content, compressive strength, flexural strength, fracture energy, freezing-thawing, porosity parameter, and scanning electron microscope—were conducted for rubberized concretes. From experiments, we can see that fresh concrete properties decreased when crumb rubber content has increased. Mostly it is related to crumb rubber (CR) lower specific gravity nature and higher fineness compared with changed fine aggregate-sand. In this research, we obtained a slight loss of compressive strength when CR was used in concrete However, these rubberized concretes with a small amount of rubber provided sufficient compressive strength results (greater than 50 MPa). Due to the pozzolanic reaction, we see that compressive strength results after 56 days in glass powder modified samples increased by 11–13% than 28 days com-pressive strengths, while at the same period control samples increased its compressive strength about 2.5%. Experiments have shown that the flexural strength of rubberized concrete with small amounts of CR increased by 3.4–15.8% compared to control mix, due the fact that rubber is an elastic material and it will absorb high energy and perform positive bending toughness. The test results indicated that CR can intercept the tensile stress in concrete and make the deformation more plastic. Fracturing of such conglomerate concrete is not brittle, there is no abrupt post-peak load drop and gradually continues after the maximum load is exceeded. Such concrete requires much higher fracture energy. It was obtained that FCR particles (lower than A300) will entrap more micropores content than coarse rubbers because due to their high specific area. Freezing-thawing results have confirmed that Kf values can be conveniently used to predict freeze-thaw resistance and durability of concrete. The test has shown that modification of concrete with 10 kg fine rubber waste will lead to similar mechanical and durability properties of concrete as was obtained in control concrete with 2 kg of prefabricated air bubbles. [ABSTRACT FROM AUTHOR]