Abstract: Optical properties of PbS quantum dots (QDs) precipitated inside the oxide glass matrix were investigated. Photoluminescence (PL) from the PbS QDs showed peak wavelengths located at 1170–1680nm with widths of 150–550nm. Radii of QDs in glasses were 2.3–4.7nm depending upon the thermal treatment. Peak wavelengths of PL bands shifted as much as 70nm as the temperatures and excitation irradiances increased. Calculated effective local temperatures indicated that these shifts of PL spectra were associated with local heating induced by the temperatures and laser beam. [Copyright &y& Elsevier]

Abstract: Thermal treatment at 480 °C for 40 h resulted in the precipitation of β-PbF2 nano-crystals inside the oxy-fluoride glasses co-doped with Ho3+, Tm3+ and Yb3+. Generation of white light was achieved through the simultaneous blue, green and red up-converted emissions by pumping at 900 nm. Simulation of sunlight was most successfully achieved with pump power of ∼150 mW. [Copyright &y& Elsevier]

Abstract: Transparent nano-crystalline glass–ceramics (nano-structured glasses) were prepared from oxy-fluoride precursor glass doped with HoF3 and their luminescence properties were investigated. Visible blue, green and red emissions were observed, and the relative intensity of the green and red emission was strongly dependent on HoF3 concentration. Under 750 nm pumping, the intense green emission due to the photon avalanche process was observed at room temperature from nano-structured glass doped with high (0.5mol%) concentration of HoF3. [Copyright &y& Elsevier]

Abstract: CdSe quantum dots (QDs) were precipitated in silicate glasses under various durations and temperatures of heat-treatment. Absorption and photoluminescence (PL) spectra of the QDs showed the quantum confinement effect from CdSe QDs. When the glass was heat-treated for 10h, estimated average QD sizes increased from 5.2nm when the glass was heat-treated at 490°C and to 6.9nm when it was treated at 500°C. When the glass was heat-treated at 480°C, estimated average QD sizes were 4.9nm after 20h and 5.3nm after 30h. The PL peak position was independent of the excitation wavelengths; this result indicates that the size distribution of CdSe QDs was narrow. [ABSTRACT FROM AUTHOR]