Search

Direct coagulation casting of alumina via controlled release of high valence counter ions using ammonium polyphosphate (APP) chelate complex as the coagulating agent was proposed. APP chelate complex suspension was prepared from APP and calcium chloride. Calcium used as high valence counter ions was chelated by APP. The average particle size of the chelate complex is 0.13 μm with a narrow particle size distribution which is close to the size of alumina particles. Glycerol diacetate was used to tailor the pH value of the suspension by hydrolysis which produces acetic acid. The lowering of the pH value helps to decompose the chelate complex, and enhance to release the calcium chelated. It is indicated that the viscosity of the suspensions with the addition of APP chelate complex suspension and glycerol diacetate increases to approximately 20 Pa s after heating at 40–70 °C for 1.5–5 h, which is high enough to coagulate the suspension. 55 vol% alumina suspension with a addition of 3 vol% APP chelate complex suspension and 5 vol% glycerol diacetate treated at 60 °C could coagulate completely within 2 h with a compressive strength of 2.1 MPa. Dense alumina with a relative density of above 97% and a flexural strength of 388 ± 23 MPa can be prepared by this method from 55 vol% alumina suspensions without a burnout process. [ABSTRACT FROM PUBLISHER]

Ceramics with high strength and reliability are highly demanded in engineering applications. In this paper, a modified direct coagulation casting via high valence counter ions (DCC-HVCI) method for alumina using calcium citrate complex assisted by glycerol diacetate was investigated. Calcium citrate complex suspensions were prepared by mixing tri-ammonium citrate and calcium chloride in water. Effect of reaction time on the chelating properties of the prepared suspensions was investigated. Concentrated alumina suspensions with a solid loading of 50 vol% were prepared by mixing the calcium citrate complex suspensions and alumina powder at pH of 10.5. Then the suspensions were coagulated by adding 3–6 vol% glycerol diacetate at temperatures of 40–70 °C for 2–6 h. The compressive strength of the coagulated wet samples is in the range 1.1–2.4 MPa. Alumina ceramics sintered at 1550 °C shows homogeneous microstructures with flexural strength and Weibull modulus of 455±17 MPa and 30, respectively. [ABSTRACT FROM AUTHOR]

A direct coagulation casting method for silicon nitride suspension via dispersant reaction was reported. Tetramethylammonium hydroxide (TMAOH) was used as dispersant to prepare silicon nitride suspension with high solid loading and low viscosity. Influences of TMAOH and pH value on the dispersion of silicon nitride powder were investigated. Glycerol diacetate (GDA) was used to coagulate the silicon nitride suspension. Influences of the concentration of glycerol diacetate on the viscosity and pH value of the suspension were investigated. It was indicated that high viscosity sufficient to coagulate the suspension was achieved by adding 1.0–2.0 vol% glycerol diacetate at 40–70 °C. The coagulation mechanism was proposed that the silicon nitride suspension was destabilized by dispersant reacting with acetic acid which was hydrolyzed from glycerol diacetate at elevated temperature. Coagulated samples could be demolded without deformation by treating 50 vol% silicon nitride suspensions with 0.2 wt% tetramethylammonium hydroxide and 1.0–2.0 vol% glycerol diacetate at different temperatures. Dense silicon nitride ceramics with relative density above 98.8% had been prepared by this method using glycerol diacetate as coagulating agent sintered by different methods. [ABSTRACT FROM AUTHOR]

Direct coagulation casting via controlled release of high valance counter ions (DCC-HVCI) has been reported in recent years. In this paper, concentrated yttria-stabilized zirconia (YSZ) suspensions were coagulated using DCC-HVCI method with magnesium citrate as coagulating agent assisted by pH shift in the presence of glycerol diacetate. The effect of ammonium polyacrylate (PAA-NH 4 ) on the dispersibility of YSZ powder was investigated. The influence of concentrations of glycerol diacetate and magnesium citrate on pH and viscosities of YSZ suspensions was studied. The results indicate that concentrated YSZ suspensions can be coagulated by adding 2 vol% glycerol diacetate and magnesium citrate above 0.5 wt% at room temperature for 2–5 h. The compressive strength of coagulated wet samples is above 2.0 MPa. YSZ ceramics sintered at 1450 °C show homogeneous microstructures with relative densities of 98.9–99.2%. Flexural strength of YSZ ceramics is 869±84 MPa. [ABSTRACT FROM AUTHOR]