The deposition of Mn(12) single molecule magnets on gold surfaces was studied for the first time using combined X-ray absorption spectroscopy (XAS) and X-ray magnetic circular dichroism (XMCD) methods at low temperature. The ability of the proposed approach to probe the electronic structure and magnetism of Mn(12) complexes without significant sample damage was successfully checked on bulk samples. Detailed information on the oxidation state and magnetic polarization of manganese ions in the adsorbates was obtained from XAS and XMCD spectra, respectively. Partial reduction of metal ions to Mn(II) was clearly observed upon deposition on Au(111) of two different Mn(12) derivatives bearing 16-acetylthio-hexadecanoate and 4-(methylthio)benzoate ligands. The average oxidation state, as well as the relative proportions of Mn(II), Mn(III) and Mn(IV) species, are strongly influenced by the deposition protocol. Furthermore, the local magnetic polarizations are significantly decreased as compared with bulk Mn(12) samples. The results highlight an utmost redox instability of Mn(12) complexes at gold surfaces, presumably accompanied by structural rearrangements, which cannot be easily revealed by standard surface analysis based on X-ray photoelectron spectroscopy and scanning tunnelling microscopy.

In a proof-of-principle study, a soluble macrocyclic single-molecule magnet (SMM) containing a CuII3TbIII magnetic core was covalently grafted onto small gold nanoparticles pre-functionalised with carboxylate-terminated tethers. A modified microemulsion method allowed production of the small and monodisperse nanoparticles (approximately 3.5 nm in diameter) for the chemisorption of a large amount of intact macrocyclic complexes in the hybrid system. [ABSTRACT FROM AUTHOR]

A comfortable environment: Interaction with a gold surface fully preserves the spin structure of a Fe3Cr single‐molecule magnet of current interest in molecular spintronics. Magnetic polarization at metal sites is measured over a broad temperature range (from 10 to 300 K) by X‐ray magnetic circular dichroism (XMCD), which provides the required monolayer sensitivity. The data are used to evaluate FeCr superexchange coupling interactions, which compare well with bulk‐phase values in both sign and strength (see figure). [ABSTRACT FROM AUTHOR]