Abstract: A thermodynamic study on Li-poor vapor transport equilibration (VTE) in MgO-doped LiNbO3 crystal was carried out. A thorough thermodynamic VTE model is established that considers all of possible factors including the depth relative to crystal surface, VTE temperature and time. To solve the model, the composition on crystal surface was studied as a function of VTE temperature and time. To achieve that, a number of Li-deficient MgO(5 mol% in melt):LiNbO3 crystals were produced by the VTE under different temperatures from 1010 to 1130 °C for different durations up to 395 h, the crystalline phase contained was determined by X-ray powder diffraction and their surface compositions were determined from the measured birefringence. The results show that the Li-deficient crystal keeps the LiNbO3 phase. The surface Li2O-content has an Arrhenius relationship to the VTE temperature and a square-root dependence on the VTE duration. Based upon the VTE temperature and time dependences of surface Li2O-content, the solution to the thermodynamic VTE is obtained and verified experimentally. The solution is crucial to design and produce a Li-deficient MgO:LiNbO3 crystal with desired Li2O-content profile. By using the solution, one can predict the Li2O-content depth profile after a certain VTE time for a given VTE temperature. [Copyright &y& Elsevier]

Abstract: Rare-earth-doping and various post-growth heat treatments effects on OH− absorption in singly Er- and Yb-doped, doubly Er/Mg- and Er/Yb-doped LiNbO3 crystals have been investigated. The OH− absorption in the rare-earth-doped crystals shows definite anisotropy and is stronger in a Z-cut plate. Rare-earth-doping causes considerable OH− absorption reduction. MgO-codoping induces additional reduction. Slight/heavy rare-earth-doping causes slight/considerable spectral shape change. Thermal reduction treatment causes OH− absorption vanishing whether the crystal is originally congruent or near-stoichiometric. Further oxidation treatment renders the absorption reemerged. Li-rich vapor transport equilibration (VTE) treatment causes significant absorption decrease. For a slightly rare-earth-doped Li-rich VTE-treated crystal, its spectral feature is similar to that of the undoped near-stoichiometric crystal; for a heavily rare-earth-doped VTE-treated crystal, its spectral shape preserves the feature of the heavily rare-earth-doped as-grown crystal. For the Er/Mg-codoped crystal studied, the Li-rich VTE also induces an abrupt conversion of peaking position from 3483 cm−1 to 3535 cm−1. The absorption in the Li-rich VTE-treated crystals also reveals aging effects in spectral shape, peaking position and absorption intensity. Li-poor VTE induces significant absorption increase. In addition, the effect of OH− presence on lifetime of Er3+ emission at 1.5 μm was also studied. The results show that the effect is small for the as-grown congruent crystals and slight for Li-rich VTE-treated ones. [Copyright &y& Elsevier]