Search

Abstract: A two-step route comprising treatment in sodium aluminate followed by acid washing was developed to introduce secondary mesoporosity in ZSM-5 zeolites with different Si/Al ratios. The parent and treated zeolites were characterized by ICP-OES (solids and filtrates), XRD, TGA, TEM, gas adsorption (N2 at 77K and Ar at 87K), FTIR, and NH3-TPD. The contact of the zeolite with NaAlO2 solutions induced mild leaching of framework silicon, viz. desilication. However, the porosity of the resulting samples was mostly blocked by NaAlO2-derived deposits and Si-containing debris. A subsequent acid washing with HCl or oxalic acid removed the blocking species, largely regaining the native microporosity and further uncovering the extensive intracrystalline mesoporosity generated in the first step. In order to maximize the micro- and mesoporosity in the final zeolites, the conditions of the NaAlO2 and acid treatments were varied with respect to concentration, temperature, and time. The efficiency of the two-step treatment was remarkable for zeolites with Si/Al=25 and 40. The mesopore surface area of the hierarchical ZSM-5 was 3–4 times higher than in the parent zeolites, while other intrinsic properties like crystallinity and acidity were largely preserved. The physico-chemical properties of hierarchical ZSM-5 obtained by the two-step route and by conventional desilication in NaOH were compared. Both desilication variants led to equivalent mesopore surface areas, although the two-step route presented a higher solid yield and produced smaller mesopores due to the much lower amount of silicon leached compared to the treatment in sodium hydroxide. Mechanistic and kinetic aspects of silicon dissolution and porosity development in ZSM-5 were discussed on the basis of alkaline treatments in mixtures of NaOH and NaAlO2. [Copyright &y& Elsevier]

The establishment of suitable processes for the conversion of glycerol into allyl alcohol is hindered by the fast deactivation of solid acids in the dehydration of the substrate to acrolein and by the requirement of hydrogen donors to enhance the selectivity of the subsequent reduction step. In this work, silver nanoparticles deposited onto a hierarchical ZSM-5 zeolite are proved to be an effective bifunctional catalyst to conduct the two reactions in the gas phase and in the presence of hydrogen by using a continuous fixed-bed reactor. The acidic function was accomplished by using a ZSM-5 zeolite modified by facile alkaline and acid treatments, which decreased the amount of Lewis acid centers while preserving the amount of Brønsted acid centers, and introduced an auxiliary network of intracrystalline mesopores, thus boosting the selectivity to acrolein (62 %) and the resistance to coking. Upon screening of various metals supported on the aluminosilicate, silver was identified as a superior hydrogenation catalyst, enabling a relatively high activity with >50 % allyl alcohol selectivity. Tuning of the metal loading, temperature, pressure, and contact time led to 15 % yield of allyl alcohol, thus approaching the state-of-the-art transfer hydrogenation systems, and stable behavior for 100 h on stream. Our results highlight the advantage of conducting the two transformations over a bifunctional material rather than over two separate single-function solids. [ABSTRACT FROM AUTHOR]

An exact knowledge of the architecture of complex pore networks and the impact on transport processes is critical to understand and optimize their integration in many functional solids. Here, a robust and versatile approach is demonstrated to quantitatively map pore constrictions within hierarchical faujasite-type (Y and USY) zeolites, the most widely applied zeolitic materials in industry. Differential hysteresis scanning measurements by high-resolution argon sorption coupled with an advanced modeling framework enable the derivation of the amount and size of pyramidal, constricted, and occluded mesopores. This yields unprecedented insight into the impact of widely practiced demetallation treatments on the porosity evolution and clearly highlights the interplay between the geometry of mesopores developed by a given treatment and those introduced by previously applied postsynthetic modifications. Based on the findings, the dynamic assessment by positron annihilation spectroscopy confirms the effectiveness of each mesopore type at enhancing the diffusion of ortho-positronium within the crystal. The quantitative descriptors attained by these complementary techniques can revolutionize the design of porous materials for a wide range of applications. [ABSTRACT FROM AUTHOR]

Abstract: The improvement of molecular transport properties of hierarchical H-ZSM-5 obtained by desilication was evidenced by studying the desorption of o-xylene and isooctane by in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). This technique enabled monitoring simultaneously bands associated with the molecular probes and the zeolite, using powdered sample masses as low as 1mg. Two H-ZSM-5 samples with markedly different crystal sizes were investigated. The first sample was commercial and consisted of small crystallites (ca. 250nm). The second sample were laboratory-made large crystals with coffin-like shape (ca. 17×4×4μm3). The hierarchical derivatives of the small and large zeolite crystals displayed 250 and 120m2 g−1 of mesopore surface area, respectively, in contrast to the 62 and 5m2 g−1 of the parent counterparts. The data based on o-xylene desorption were partly disguised by site-desorption limitations. Desorption experiments using isooctane evidenced a 4-fold reduction in the characteristic diffusion path length on both mesoporous small and large zeolites with respect to their purely microporous analogues. These results confirm the substantial potential for improvement of commercial nanocrystalline zeolites in diffusion-limited reactions upon the introduction of intra-crystalline mesoporosity by post-synthesis modification. [Copyright &y& Elsevier]

Abstract: Desilication of ITQ-4 (IFR code, 1-dimensional 12-MR channel system of 0.62nm×0.72nm) in aqueous NaOH solutions was practiced in order to produce the zeolite in the hierarchical form, i.e. combining the native micropores with a secondary network of intracrystalline mesopores. The parent material (Si/Al=32) was synthesized using benzylquinuclidinium as the structure-directing agent in the presence of fluoride anions. The samples were characterized by ICP-OES, XRD, TEM, N2 adsorption, and FTIR spectroscopy. In a representative treatment, the mesopore surface area of the ITQ-4 experienced a sevenfold increase (from 29 to 206m2 g−1) upon optimized NaOH post-treatment, whereas the microporosity was reduced by 70% (from 0.20 to 0.06cm3 g−1). Chemical analysis and infrared spectroscopy of adsorbed pyridine showed that after alkaline treatment the amount of Brønsted acid sites remains practically constant whereas a significant increase in Lewis acid sites was obtained. Infrared studies with adsorbed 2,4,6-collidine concluded that the accessibility of acid sites in the hierarchical zeolite increased substantially due to an increase in the available active sites at the pore mouths of the hierarchical zeolite. [Copyright &y& Elsevier]

Abstract: Desilication in alkaline medium is demonstrated as a general route to synthesize hierarchical metallosilicate zeolite crystals with preserved crystallinity. The lattice trivalent cation (not only Al3+ but also Ga3+, Fe3+, and B3+) regulates the alkaline-assisted hydrolysis of silicon towards controlled mesoporosity development. This finding widens the family of modified zeolite compositions that integrate in a single crystalline material micropores and mesopores and enables better accessibility in catalytic applications compared to the purely microporous counterparts. [Copyright &y& Elsevier]

An accessibility index (ACI) was derived from infrared spectroscopy of substituted alkylpyridines with different size (pyridine: 0.57nm, 2,6-lutidine: 0.67nm, and 2,4,6-collidine: 0.74nm) over hierarchical porous ZSM-5 crystals. The samples were prepared by selective silicon extraction of a commercial sample in NaOH (desilication), and they contained different degrees of intracrystalline mesoporosity. Our results demonstrate the enhanced accessibility of Brønsted acid sites in the hierarchical zeolites. For example, a relatively bulky molecule such as collidine, which probes practically no acid site of the parent medium-pore MFI structure, can access up to 40% of the acid sites in the mesoporous sample. The ACI is a powerful tool to standardize acid site accessibility in zeolites, and can be used to rank the effectiveness of synthetic strategies to prepare hierarchical zeolites. [Copyright &y& Elsevier]

On page 5621, J. Kenvin, J. Pérez‐Ramírez, and coworkers demonstrate differential hysteresis scanning by high‐resolution argon sorption and positron annihilation spectroscopy as powerful tools to quantify the complex architecture of pore networks in hierarchical faujasite zeolites and their efficiency in transport processes. The descriptors attained by these complementary techniques further advance the design of porous materials for a wide range of applications. The creatures in the cover, exploring a tortious cave system, exemplify the challenges with pore accessibility and connectivity. [ABSTRACT FROM AUTHOR]