The thermal modification of wood in a nitrogen atmosphere shapes the functional properties of wood. The aim of this research was to determine the influence of different levels of temperature and the duration of thermal modification on the mechanical properties of the black poplar (Populus nigra L.). Black poplar was thermally modified in nitrogen atmosphere in the temperature range from 160 °C to 220 °C (6 levels) for 2 h to 8 h (4 levels), resulting in a total of 24 treatments. The effect of these treatments on compressive strength parallel to the grain (CS), modulus of rupture (MOR), and modulus of elasticity during bending (MOE) were analyzed. Thermal modification influenced the mechanical properties of black poplar wood. After thermal modification occurred in a nitrogen atmosphere, an increase in compressive strength was noticeable for all variants of black poplar wood modification. The highest 16% increase in CS was obtained for the modification carried out at the temperature of 160 °C and for 2 h. An increase was also found for MOE when modified under mild conditions, while a decrease occurred for variants at higher temperatures, i.e., for 200 °C and 220 °C. The study showed that for all modification variants, there was a decrease in MOR alongside the increase in modification temperature and time. [ABSTRACT FROM AUTHOR]

Black poplar (Populus nigra L.) was thermally modified in nitrogen atmosphere. The effects of the modification process on poplar wood were evaluated for temperatures: 160 °C, 190 °C, and 220 °C applied for 2 h; and 160 °C and 190 °C for 6 h. The percentual impact of temperature and time of modification on the properties of modified wood was analysed. The study permitted the identification correlations between the chemical composition and selected physical properties of thermally modified poplar wood. The dimensional stability of poplar wood was improved after thermal modification in nitrogen. The higher the temperature of modification, the lower the equilibrium moisture content (EMC) of black poplar. At the temperature of 220 °C, EMC was two times lower than the EMC of non-modified black poplar. It is also possible to reduce the dimensional changes of wood two-fold (at the modification temperature of 220 °C), both in radial and tangential directions, independently of the acclimatization conditions (from 34% to 98% relative humidity, RH). Similar correlations have been found for wood that has been soaked in water. Higher modification temperatures and longer processing times contributed to a lower swelling anisotropy (SA). [ABSTRACT FROM AUTHOR]