The present work is focused on developing Ti-xTa porous alloys processed by the space holder method and solid-state sintering. The volume fraction of Ta ranged between 20 and 30 wt.%. The sintering kinetics was evaluated by dilatometry tests. Sintered materials were characterized by SEM, XRD and computed tomography. Porosity features and permeability were determined from 3D images, and their mechanical properties were evaluated from microhardness and compression tests. The sintering behavior and the final microstructure are driven by the Ta diffusion into the Ti, slowing down the densification and modifying the transition temperature of α-to-β. Due to β-stabilization, martensite α′ was obtained after sintering. Mechanical properties are reduced because of the β-stabilization and pore addition, being predominantly the pore effect. Permeability depended on the pore characteristics, finding values close to the human bones. It was concluded that powder metallurgy generates highly TixTa alloys with a combination of α, β and α′ Ti phases as well as remaining Ta particles that are beneficial to improve the biocompatibility and osseointegration of such materials. Being the Ti25Ta40salt alloy the most suitable for orthopedic implants because of its characteristics and properties. [ABSTRACT FROM AUTHOR]

We present a novel Ti64/20Ag highly porous composite fabricated by powder metallurgy for biomedical applications and provide an insight into its microstructure and mechanical proprieties. In this work, the Ti64/20Ag highly porous composites were successfully fabricated by the space holder technique and consolidated by liquid phase sintering, at lower temperatures than the ones used for Ti64 materials. The sintering densification was evaluated by dilatometry tests and the microstructural characterization and porosity features were determined by scanning electron microscopy and computed microtomography. Permeability was estimated by numerical simulations on the 3D real microstructure. Mechanical properties were evaluated by simple compression tests. Densification was achieved by interparticle pore filling with liquid Ag that does not drain to the large pores, with additional densification due to the macroscopical deformation of large pores. Pore characteristics are closely linked to the pore formers and the permeability was highly increased by increasing the pore volume fraction, mainly because the connectivity was improved. As expected, with the increase in porosity, the mechanical properties decreased. These results permitted us to gain a greater understanding of the microstructure and to confirm that we developed a promising Ti64/20Ag composite, showing E of 7.4 GPa, σy of 123 MPa and permeability of 3.93 × 10−11 m2. Enhanced adaptability and antibacterial proprieties due to Ag were obtained for bone implant applications. [ABSTRACT FROM AUTHOR]