Search

This research investigates the long-term shrinkage and Relative Mass Loss (RML) of mature Portland concretes (pure CEMI and blended CEMV/A), at temperatures of 20°C and 80°C. When placed at 80°C and at relative humidities (RH) below 50-60%, concrete shrinkage increases with very slow stabilization kinetics by several hundreds of μm/m, while RML remains of about 0.2%. The origins of this continued shrinkage, simultaneously with limited RML, are investigated through the changes in (i) the pore structure of the concretes (by Mercury Intrusion Porosimetry and nitrogen adsorption) and in (ii) their solid phases (by TGA/DTA, FTIR spectroscopy coupled to DVS, quantitative X-Ray Diffraction by Rietveld analysis, and 29Si and 27Al MAS NMR). While the pore structure coarsens during continued shrinkage, several phase transformations occur, namely ettringite decomposition and changes in the silicate chain length of the C-A-S-H. While these structural changes are documented, their relationship with shrinkage/RML and to the pore structure is novel. [ABSTRACT FROM AUTHOR]

An experimental campaign was carried out to study the passivity of steel embedded in blended cement paste. Mockup samples made of steel coupons (milled or pre-corroded) embedded in cement paste were tested under controlled relative humidity or in a solution simulating clay underground water and under aerated and de-aerated conditions, during up to 3 years. The results of gravimetric measurements show that the average corrosion rates determined on milled coupons are lower than 1 µm/year and vary from 0.2 to 2.7 µm/year for pre-corroded coupons. An apparent passive corrosion state is reached rapidly whatever the environmental conditions. Moreover, solid characterisations (Raman spectroscopy and SEM-EDS) point to a stable state in terms of the nature of the corrosion products and of the composition of the steel/cement paste interface. These results are similar to the ones previously obtained for steel coupons embedded in Portland cement mortar. This paper is part of a supplement on the 6th International Workshop on Long-Term Prediction of Corrosion Damage in Nuclear Waste Systems. [ABSTRACT FROM AUTHOR]

Abstract The impact of temperature on carbonation was investigated in laboratory conditions using a device developed for this purpose. Two hardened cement pastes (CEM I and CEM V/A) were tested between 20 °C and 80 °C at different levels of relative humidity (RH). The carbonation rate of the CEM I increased with temperature, whereas that of CEM V/A reached a maximum at around 50 °C. [ABSTRACT FROM AUTHOR]

The influence of atmospheric carbonation on gas diffusion was investigated using four hardened cement pastes (CEM I, CEM III/A, CEM V/A, and a low-alkalinity binder) with common water-to-binder ratio (0.4). The diffusivity of the non‑carbonated and carbonated pastes with respect to helium and nitrogen was measured at different relative humidities. Carbonation decreased the diffusivity of the CEM I paste, whereas that of the other binders significantly increased after carbonation. These results show the competition between porosity clogging and cracking induced by carbonation. The consequences of carbonation are therefore believed to depend on the considered binder. Clogging dominates in ordinary Portland cement (OPC), leading to a decrease in its transport properties after carbonation; cracking dominates in blended cements, leading to a significant increase in its transport properties after carbonation. [ABSTRACT FROM AUTHOR]