Search

The synergistic flame retardant system consisted of intumescent flame retardant (IFR) and organic modified attapulgite (OATP) synergist was used to improve the mechanical properties and flame retardancy of continuous glass fibre reinforced polyethylene composites (GFPE). The IFR was composed of ammonium polyphosphate (APP) as acid source and poly(1,3-diaminopropane-1,3,5-triazine-o-bicyclic pentaerythritol phosphate) (PDTBP) as carbon source. The mechanical properties (tensile strength) of GFPE/IFR/OATP were improved by 35%–43% after adding OATP synergist with rod-like fiber structure due to its strengthening and toughening effect on the resin matrix, and the flame retardancy increased first and then decreased with the increase of OATP synergist loading. When 4 wt% OATP synergist was added into GFPE/IFR, the LOI value increased from 29.5% to 31.3% and the flame spread rate significantly reduced. The synergistic flame retardant system of IFR/OATP could form a stable and dense char layer on the surface of glass fibre and weaken the wicking actions of glass fibre. The synergistic flame retardant system of 26 wt% IFR/4 wt% OATP could endow GFPE with best comprehensive performance. [ABSTRACT FROM AUTHOR]

A novel intumescent flame retardant (IFR) system composed of ammonium polyphosphate and poly (1,3-diaminopropane-1,3,5-triazine-o-bicyclic pentaerythritol phosphate) (APP/PDTBP) was mixed with polyethylene to prepare the continuous glass fibre reinforced polyethylene (CGF/PE) unidirectional prepregs by melt impregnation process, and then the CGF/PE/IFR composite laminate were consolidated by hot compression moulding method. The flame retardancy, thermal stability and mechanical properties of CGF/PE/IFR composite laminates were investigated by limiting oxygen index, vertical burning test, cone calorimetric test, thermogravimetric analysis, tensile and flexural strength tests, mode I interlaminar fracture toughness test, and scanning electron microscopy (SEM). The flame retardancy of CGF/PE composite laminates increased with the increase of IFR system loading, which attributes to the formation of intumescent char layer from flame retardants and the weakening of wicking actions of glass fibres. The mechanical properties increased and then decreased with addition of flame retardants, except for the flexural strength with continuous increase. The SEM images showed that IFR system had toughening effect and could improved the strength of fibre-matrix interface. Based on the mechanical properties and the flame retardancy, when the matrix contains 30 wt% IFR system, the CGF/PE/IFR composite laminate had the best comprehensive performance. Image 1 [ABSTRACT FROM AUTHOR]

In this work, a novel phosphorous–nitrogen based charring agent named poly(1,3-diaminopropane-1,3,5-triazine-o-bicyclic pentaerythritol phosphate) (PDTBP) was synthesized and used to improve the flame retardancy of high-density polyethylene (HDPE) together with ammonium polyphosphate (APP). The results of Fourier transform infrared spectroscopy (FTIR) and 13C solid-state nuclear magnetic resonance (NMR) showed that PDTBP was successfully synthesized. Compared with the traditional intumescent flame retardant (IFR) system contained APP and pentaerythritol (PER), the novel IFR system (APP/PDTBP, weight ratio of 2:1) could significantly promote the flame retardancy, water resistance, and thermal stability of HDPE. The HDPE/APP/PDTBP composites (PE3) could achieve a UL-94 V-0 rating with LOI value of 30.8%, and had a lower migration percentage (2.2%). However, the HDPE/APP/PER composites (PE5) had the highest migration percentage (4.7%), lower LOI value of 23.9%, and could only achieve a UL-94 V-1 rating. Besides, the peak of heat release rate (PHRR), total heat release (THR), and fire hazard value of PE3 were markedly decreased compared to PE5. PE3 had higher tensile strength and flexural strength of 16.27 ± 0.42 MPa and 32.03 ± 0.59 MPa, respectively. Furthermore, the possible flame-retardant mechanism of the APP/PDTBP IFR system indicated that compact and continuous intumescent char layer would be formed during burning, thus inhibiting the degradation of substrate material and improving the thermal stability of HDPE. [ABSTRACT FROM AUTHOR]