Search

As gallium oxide-based heterojunction devices gain prominence, low-resistance contacts to aluminum gallium oxide material are of increasing importance for high performance and access to modulation doped layers. Here, the activation of ion-implanted silicon donors is investigated as a function of donor density from 5 × 1018 cm−3 to 1 × 1020 cm−3, activation anneal duration from 6 s to 600 s, and activation temperature from 900°C to 1140°C. Importantly, ohmic behavior was achievable across a reasonably wide process window at moderate to high doping concentrations. Specific contact resistance of 1 × 10−3 Ω cm2 and sheet resistance of 2.8 kΩ/□ were achieved for a 60 nm-deep 1 × 1020 cm−3 box implant after activation at 1000°C for 6 s with standard Ti/Au contacts. Under these conditions, an activation efficiency of 7% was observed with Hall mobility of ~32 cm2/Vs. Furthermore, we demonstrate a Schottky diode formed of implanted material with a rectification ratio > 106 and further confirm the Hall carrier density results using capacitance–voltage profiling analysis. Finally, we show the significant impact of anneal duration and the potential for deleterious over-annealing which reduces the active carrier density, mobility, and resultant material conductivity. [ABSTRACT FROM AUTHOR]

Codoping of gallium nitride for improved acceptor ionization has long been theorized; however, reduction to practice proves difficult via growth. Herein, implementation of codoping via ion implantation and symmetric multicycle rapid thermal annealing utilizing magnesium codoped with silicon or oxygen is demonstrated. Results show enhanced photoluminescence with both donor species but with an order of magnitude greater increase with concurrent p‐type hall for codoping with oxygen. Furthermore, the addition of nitrogen to balance stoichiometry suppresses defect photoluminescence signals. The incorporation of the donor and nitrogen demonstrates defect reduction beyond magnesium, only implants despite the additional implant dose and resultant damage with coimplantation. The enhanced hole concentrations evident with oxygen incorporation reveal important considerations for device design given unintentional doping during growth and future incorporation of ion implantation capabilities. [ABSTRACT FROM AUTHOR]

Selective area doping via ion implantation is crucial to the implementation of most modern devices and the provision of reasonable device design latitude for optimization. Herein, we report highly effective silicon ion implant activation in GaN via Symmetrical Multicycle Rapid Thermal Annealing (SMRTA) at peak temperatures of 1450 to 1530 °C, producing a mobility of up to 137 cm2/Vs at 300K with a 57% activation efficiency for a 300 nm thick 1 × 1019 cm−3 box implant profile. Doping activation efficiency and mobility improved alongside peak annealing temperature, while the deleterious degradation of the as-grown material electrical properties was only evident at the highest temperatures. This demonstrates efficient dopant activation while simultaneously maintaining low levels of unintentional doping and thus a high blocking voltage potential of the drift layers for high-voltage, high-power devices. Furthermore, efficient activation with high mobility has been achieved with GaN on sapphire, which is known for having relatively high defect densities but also for offering significant commercial potential due to the availability of cheap, large-area, and robust substrates for devices. [ABSTRACT FROM AUTHOR]

Ion implantation of magnesium for p‐type GaN presents many opportunities; however, activation has proven difficult due to the decomposition of GaN at relevant annealing temperatures. Herein, testing the efficacy of multiple in situ and ex situ caps based on aluminum nitride and silicon nitride for GaN protection during annealing is presented. Photoluminescence shows better activation for in situ metal organic chemical vapor deposition (MOCVD)‐grown aluminum nitride caps compared with ex situ sputtered aluminum nitride and the best performance by ex situ plasma‐enhanced chemical vapor deposition (PECVD) silicon nitride. Furthermore, only samples annealed at the highest temperatures tested show preferential growth of UV luminescence to yellow‐green luminescence reinforcing the need for better capping solutions and higher temperature annealing. [ABSTRACT FROM AUTHOR]

We report selective area n-type doping using ion implantation of Si into semi-insulating, C-doped GaN samples activated using both conventional rapid thermal annealing (RTA) and 30 atm N2 overpressure annealing. Implanted regions were tested for Si activation using Circular Transmission Line Measurements (CTLM), while linear and circular photoconductive switches (PCSS) in the unimplanted regions were used as a test vehicle to separate implanted Si dopant activation from leakage paths generated by N vacancy formation due to damage and decomposition during annealing. We observed that at an optimal temperature around 1060 °C, a low contact resistivity of $1\times 10^{-6}\,\,\Omega $ -cm2 was obtained while preserving the breakdown of the unimplanted regions. [ABSTRACT FROM AUTHOR]