Ion implantation of magnesium for p‐type GaN presents many opportunities; however, activation has proven difficult due to the decomposition of GaN at relevant annealing temperatures. Herein, testing the efficacy of multiple in situ and ex situ caps based on aluminum nitride and silicon nitride for GaN protection during annealing is presented. Photoluminescence shows better activation for in situ metal organic chemical vapor deposition (MOCVD)‐grown aluminum nitride caps compared with ex situ sputtered aluminum nitride and the best performance by ex situ plasma‐enhanced chemical vapor deposition (PECVD) silicon nitride. Furthermore, only samples annealed at the highest temperatures tested show preferential growth of UV luminescence to yellow‐green luminescence reinforcing the need for better capping solutions and higher temperature annealing. [ABSTRACT FROM AUTHOR]

This letter demonstrates vertical GaN junction barrier Schottky (JBS) rectifiers fabricated with novel ion implantation techniques. We used two different methods to form the lateral p-n grids below the Schottky contact: 1) Mg implantation into n-GaN to form p-wells and 2) Si implantation into p-GaN to form n-wells. Specific differential ON-resistances ( R \mathrm{\scriptscriptstyle ON} ) of 1.5–2.5 \textm\Omega ~\cdot cm2 and 7–9 \textm\Omega ~\cdot cm2 were obtained in the Mg-implanted and Si-implanted JBS rectifiers, respectively. A breakdown voltage of 500–600 V was achieved in both devices, with a leakage current at high reverse biases at least 100-fold lower than conventional vertical GaN Schottky barrier diodes. The impact of n-well and p-well widths on the R \mathrm{\scriptscriptstyle ON} and BV was investigated. Fast switching capability was also demonstrated. This letter shows the feasibility of forming patterned p-n junctions by novel ion implantation techniques, to enable high-performance vertical GaN power devices. [ABSTRACT FROM AUTHOR]