Abstract: In this paper, single crystal of ytterbium (Yb) doped Ca5(PO4)3F (FAP) has been grown along the c-axis by using the Czochralski method. The segregation coefficients of Yb3+ in the Yb:FAP crystal has been determined by ICP-AES method. The absorption spectrum, fluorescence spectrum and fluorescence lifetime of the Yb:FAP crystal has been also measured at room temperature. In the absorption spectra, there are two absorption bands at 904 and 982nm, respectively, which are suitable for InGaAs diode laser pumping. The absorption cross-section (σ abs) is 5.117×10−20 cm2 with an FWHM of 4nm at 982nm. The emission cross-section (σ em) is 3.678×10−20 cm2 at 1042nm. Favorable values of the absorption cross-section at about 982nm are promising candidates for laser diode (LD) pumping. [Copyright &y& Elsevier]

Abstract: For the first time, a quaternary doping system of Er3+, Yb3+, Ce3+, Na+: CaF2 single crystal was demonstrated to have high fluorescence yield in the 1.5μm region. Through a simplified model, the branching ratio of the Er3+ 4I11/2→4I13/2 transition was estimated to be improved more than 40 times by the deactivating effect of Ce3+ in the quaternary-doped CaF2 crystal with dopants of 0.2-at% Er3+ and 2.0-at% Ce3+. Owing to the broad emission bandwidth and large emission cross-section, the quaternary-doped CaF2 system shows the great potential to achieve the high laser performance in the 1.5μm region. [Copyright &y& Elsevier]

Abstract: Gd2SiO5 (GSO) single crystal codoped with Yb3+ and Er3+ (Abbr. as Er:Yb:GSO) was successfully grown by the Czochralski (CZ) method for the first time and the spectral characteristics were investigated. The absorption and fluorescence spectra were measured. The emission lifetime of the 4I13/2–Er-level was measured to be 5.84ms and the emission cross-section at 1529nm was calculated to be 1.03×10−20 cm2. The results indicate that Er:Yb:GSO is a potential laser material at ∼1.55μm wavelength region. [Copyright &y& Elsevier]