Abstract This research investigated the technical feasibility of transforming waste drill cuttings into lightweight aggregate. Drill cuttings produced from the North Sea oil field were dried, ball milled, formed into pellets and fired at temperatures between 1160 and 1190 °C. Physical properties of the manufactured lightweight aggregate, including particle density, water absorption and compressive strength, were determined. The drill cuttings had a typical evaporite composition containing high concentrations of chloride salts. This limits the potential for using the as-received drill cutting samples in lightweight aggregate production as the products formed show high levels of leaching. The addition of a washing pre-treatment to reduce the leaching of chloride ions was necessary. Washing also reduced the initial sintering temperature and improved lightweight aggregate properties. Sintering at 1180 °C produced lightweight aggregate with particle density of 1.29 g/cm³, water absorption of 3.6% and compressive strengths of 4.4 MPa. The research showed that lightweight aggregate manufacturing represents a resource efficient option for the reuse of waste drill cuttings and provides significant material saving and landfill diversion. Highlights • Beneficial reuse of waste drill cuttings in the manufacture of LWA is presented. • LWA with properties comparable to commercial products were produced. • A washing treatment was required to mitigate Cl− leaching from LWA. • The effect of washing on the physical properties of LWA is reported. [ABSTRACT FROM AUTHOR]

This study looked at the potential of bauxite residue or red mud to be used in the manufacture of lightweight aggregate in replacement of pulverised fuel ash (PFA), commonly used as a way of recycling problematic wastes. The percentage replacements of red mud with PFA were as follows: 25, 31, 38, 44 and 50%. These were blended in a mix with waste excavated clay and sewage sludge – all from the Chongqing municipality in China. Lightweight pellets were produced using a Trefoil rotary kiln and were sintered to 1200 °C. Results showed that 44% bauxite residue replacement produced lightweight pellets with the highest compressive strength, highest density and largest water holding capacity. This would be expected in materials with a low level of silicates, which causes insufficient glass phase viscosity and therefore poor bloating during firing; producing an aggregate with a higher density but with open pores that allowed for larger water absorption. All ratios of red mud aggregates were significantly reduced in pH after firing to around pH 8, and this reduced the leachability of the aggregates to levels below those set by the European landfill directive (2003/33/EC). [ABSTRACT FROM AUTHOR]