The magnetic properties and magnetocaloric effect (MCE) in the ternary intermetallic compound of EuAuGe have been investigated. The compound undergoes a second-order magnetic phase transition at its own Curie temperatures T∼33 K. A large reversible table-like MCE has been observed from 1 to 40 K, which is related to the magnetic field-sensitive magnetic phase transition. For the magnetic field changes of 0-5 and 0-7 T, the maximum values of magnetic entropy change ( $-{\Delta } S_{\mathrm {M}}^{\max }$) are evaluated to be 7.6 and 10.1 J kg K, respectively; the corresponding relative cooling power ( RCP) are 358 and 499 J kg. The present results indicate that the EuAuGe compound is a considerable candidate for low-temperature refrigeration. [ABSTRACT FROM AUTHOR]

In this work, polycrystalline oxides viz., Ho 2 CrMnO 6 (HCMO) and Er 2 CrMnO 6 (ECMO), were prepared using the sol-gel process, and their crystal structure, magnetic properties, and magnetocaloric effects (MCEs) were studied. X-ray refinement results demonstrate that both oxides exhibited the B -site disordered perovskite type structure (Pbnm space group). A ferromagnetic-paramagnetic phase transition as well as large reversible MCEs was also observed at Curie temperatures (T C) of ~6.1 and ~5.2 K for HCMO and ECMO, respectively. For a magnetic field change (ΔH) of 0–7 T, the maximum magnetic entropy change (-Δ S M), temperature-averaged entropy change (TEC 3), and relative cooling power (RCP) were estimated to be 11.03 J/kgK, 11.02 J/kgK, and 322.7 J/kg for HCMO, and 12.94 J/kgK, 12.80 J/kgK and 277.5 J/kg for ECMO. [ABSTRACT FROM AUTHOR]