Search

The magnetic and magnetocaloric properties in the equiatomic intermetallic compounds of TmZnAl and TmAgAl have been investigated. The compounds undergo a second order magnetic transition from paramagnetic to ferromagnetic state around its own Curie temperatures T C ∼2.8 K and 3.3 K for TmZnAl and TmAgAl, respectively. A considerable reversible magnetocaloric effect (MCE) was observed at low temperature. For a magnetic field change of 7 T, the maximum values of magnetic entropy change (−Δ S M max ) and relative cooling power ( RCP ) are 11.8 J/kg K and 289 J/kg for TmZnAl, respectively, and the corresponding values for TmAgAl are 14.1 J/kg K and 315 J/kg. [ABSTRACT FROM AUTHOR]

Magnetism and magnetocaloric effect in RE AgAl ( RE = Er and Ho) intermetallic compounds have been studied. Both compounds undergo a second order magnetic phase transition from paramagnetic to ferromagnetic state. A large reversible magnetocaloric effect was observed around its own Curie temperatures T C ∼ 14 and 18 K for ErAgAl and HoAgAl, respectively. For a field change of 0–7 T, the maximum magnetic entropy change reaches 13.7 and 13.8 J/kg K for RE = Er and Ho, respectively. The corresponding relative cooling powers are evaluated to be 398 and 525 J/kg. [ABSTRACT FROM AUTHOR]

The magnetic refrigeration (MR) technology by utilizing the magnetocaloric (MC) effects of magnetic solids have been realized to be a promising energy efficiency and environmentally friendly technology. Developing or discovering proper magnetic solids with promising MC performances is one of the most important tasks at present stage since a huge gap still exists between the requirement of practical MR application and the MC performances of the magnetic solids. Herein, we reported a combined theoretical and experimental investigation of the crystal structure together with the magnetic properties, magnetic phase transition (MPT) and MC performances in Gd 2 MgTiO 6 oxide. The Gd 2 MgTiO 6 is confirmed to crystalize in a B -site ordered monoclinic double perovskite (DP) crystal structure. A rather unstable antiferromagnetic (AFM) interaction with large magnetic moment and semi-conductor characteristic with the band gap of 2.977 eV have been confirmed in Gd 2 TiMgO 6 DP oxide at ground state. Giant reversible cryogenic MC effect together with excellent MC performances have been confirmed by a series of the figure of merits including the values of maximum magnetic entropy change (-Δ S M) and refrigerant capacity (RC), which are evaluated to be 46.21 J/kgK and 300.27 J/kg around 3.3 K with the magnetic change of 0–7 T, these values are much better than most of the recently reported famous cryogenic MC materials and the commercialized magnetic refrigerants gadolinium gallium garnet (GGG) as well. The observed excellent MC performances suggest that Gd 2 TiMgO 6 DP oxide is a promising candidate material for cryogenic MR applications. Graphical abstract [Display omitted]. [ABSTRACT FROM AUTHOR]

• The gallides RE 2 Rh 3 Ga (RE = Gd, Dy, Ho, Er) compounds are fabricated. • The structural, MPT and magnetocaloric properties in RE 2 Rh 3 Ga were studied. • The present RE 2 Rh 3 Ga compound are considerable for cryogenic MR. We herein provide an experimental investigation of the gallides RE 2 Rh 3 Ga (RE = Gd, Dy, Ho, Er) regarding their magnetic properties and magnetocaloric effect (MCE). All of these RE 2 Rh 3 Ga intermetallic compounds crystallized with the Mg 2 Ni 3 Si type structure, space group R– 3 m and are ordered magnetically at low temperatures. Large reversible MCEs around their own ordering temperature were observed in all RE 2 Rh 3 Ga compounds and their magnetocaloric parameters including the maximum magnetic entropy change, refrigerant capacity, and temperature-averaged entropy change are comparable to those of some recently reported candidate materials with prominent performances, making them considerable for cryogenic MR applications. [ABSTRACT FROM AUTHOR]