Search

Abstract It is well known that rare earth (RE) based intermetallic compounds reveal various interesting magnetic properties depending on the crystallized structures and the constituent elements, paving the way for potential applications in different fields. Recent progresses regarding magnetic properties and magnetocaloric effect (MCE) in ternary rare earth RE 2 T 2 X (RE = Gd-Tm; T = Cu, Ni, Co; and X = Cd, In, Ga, Sn, Al) intermetallic compounds are reviewed in this paper. Some of them exhibit excellent MCE performances which make them attractive in the field of magnetic refrigeration at low temperature. With the aim of understanding the magnetocaloric characteristics of RE 2 T 2 X compounds, the crystal structure, magnetism and magnetic phase transition are also focused. The origin of the MCE together with the physics behind and the potential application of RE 2 T 2 X compounds are thoroughly considered. Highlights • Magnetic and magnetocaloric properties in RE 2 T2X compounds are reviewed. • The RE 2 T2X compounds show four types of crystallize structures. • Some of them exhibit excellent cryogenic magnetocaloric performances. • The origin of magnetocaloric effect in RE 2 T2X compounds is discussed. [ABSTRACT FROM AUTHOR]

We reported the magnetism, magnetic phase transition behavior and magnetocaloric effect of the ternary Dy 2 CuSi 3 and Ho 2 CuSi 3 compounds. A second order magnetic phase transition from a paramagnetic (PM) to ferromagnetic (FM) state around their respective Curie temperatures were confirmed by using the magnetic measurements and rescaled magnetic entropy change curves in both compounds. A large magnetic entropy change was obtained with the absence of thermal and magnetic hysteresis loss in both compounds. The maximal magnetic entropy change (-Δ S M max ) reach 18.3 and 28.3 J/kg K for a magnetic field change of 0–70 kOe in Dy 2 CuSi 3 and Ho 2 CuSi 3 , respectively. The corresponding values of relative cooling power ( RCP ) are evaluated to be 460 J/kg and 627 J/kg, respectively. [ABSTRACT FROM AUTHOR]

The magnetic properties and magnetocaloric effect (MCE) in antiferromagnetic non-superconducting TbNiBC compound have been investigated in detail. Under low magnetic field changes and at low temperatures, the studied compound shows an inverse MCE which is due to the fact of antiferromagnetic ground state, whereas a normal reversible MCE under high magnetic field changes is observed which is related to the field-induced first-order metamagnetic transition from antiferromagnetic to ferromagnetic states. For the magnetic field change of 0-7 T the values of maximal magnetic entropy change ( $-\Delta S_{\mathrm {M}}^{\max } )$ , refrigerant capacity (RC) and relative cooling power (RCP) for the present TbNiBC are evaluated to be 11.1 J/kg/K, 225 J/kg and 296 J/kg, respectively. [ABSTRACT FROM AUTHOR]

• The gallides RE 2 Rh 3 Ga (RE = Gd, Dy, Ho, Er) compounds are fabricated. • The structural, MPT and magnetocaloric properties in RE 2 Rh 3 Ga were studied. • The present RE 2 Rh 3 Ga compound are considerable for cryogenic MR. We herein provide an experimental investigation of the gallides RE 2 Rh 3 Ga (RE = Gd, Dy, Ho, Er) regarding their magnetic properties and magnetocaloric effect (MCE). All of these RE 2 Rh 3 Ga intermetallic compounds crystallized with the Mg 2 Ni 3 Si type structure, space group R– 3 m and are ordered magnetically at low temperatures. Large reversible MCEs around their own ordering temperature were observed in all RE 2 Rh 3 Ga compounds and their magnetocaloric parameters including the maximum magnetic entropy change, refrigerant capacity, and temperature-averaged entropy change are comparable to those of some recently reported candidate materials with prominent performances, making them considerable for cryogenic MR applications. [ABSTRACT FROM AUTHOR]