The magnetic properties and magnetic entropy change of amorphousized Tm 60 Co 20 Ni 20 ribbon were systematically studied. The results indicate that the Tm 60 Co 20 Ni 20 amorphous ribbon reveals a second order magnetic transition (paramagnetic to ferromagnetic state) based on the Arrott plots and rescaled magnetic entropy change curves. A large magnetic entropy change is achieved around its Curie temperature of T C ∼6.7 K. Under the magnetic field change (Δ Η ) of 0–5 T, the maximum values of magnetic entropy change (−Δ S M max ) and relative cooling power ( RCP ) are 17.1 J/kg K and 273 J/kg, respectively. In particular, under a relative low Δ Η of 0–2 T, a large magnetic entropy change of 11.8 J/kg K reaches, making it attractive in the field of low-temperature magnetic refrigeration. [ABSTRACT FROM AUTHOR]

In this work, polycrystalline oxides viz., Ho 2 CrMnO 6 (HCMO) and Er 2 CrMnO 6 (ECMO), were prepared using the sol-gel process, and their crystal structure, magnetic properties, and magnetocaloric effects (MCEs) were studied. X-ray refinement results demonstrate that both oxides exhibited the B -site disordered perovskite type structure (Pbnm space group). A ferromagnetic-paramagnetic phase transition as well as large reversible MCEs was also observed at Curie temperatures (T C) of ~6.1 and ~5.2 K for HCMO and ECMO, respectively. For a magnetic field change (ΔH) of 0–7 T, the maximum magnetic entropy change (-Δ S M), temperature-averaged entropy change (TEC 3), and relative cooling power (RCP) were estimated to be 11.03 J/kgK, 11.02 J/kgK, and 322.7 J/kg for HCMO, and 12.94 J/kgK, 12.80 J/kgK and 277.5 J/kg for ECMO. [ABSTRACT FROM AUTHOR]