Search

High entropy alloy nanopowders were successfully prepared by liquid-phase reduction methods and their applications were preliminarily discussed. The prepared high entropy alloy nanopowders consisted of FeNi alloy spherical powders and NiFeCoCrY alloy spherical powders with a particle size of about 100 nm. The powders have soft magnetic properties, the saturation magnetization field strength were up to 5000 Qe and the saturation magnetization strength Ms was about 17.3 emu/g. The powders have the excellent property of low high-frequency loss in the frequency range of 0.3–8.5 GHz. When the thickness of the powders coating was 5 mm, the powders showed excellent absorption performance in the Ku band; and when the thickness of the powders coating was 10 mm; the powders showed good wave-absorbing performance in the X band. The powders have good moulding, and the powders have large specific surface area, so that the magnetic powder core composites could be prepared under low pressure and without coating insulators, and the magnetic powder cores showed excellent frequency-constant magnetization and magnetic field-constant magnetization characteristics. In the frequency range of 1~100 KHz; the μm of the magnetic powder core heat-treated at 800 °C reached 359, the μe was about 4.6 and the change rate of μe with frequency was less than 1%, meanwhile; the magnetic powder core still maintains constant μe value under the action of the external magnetic field from 0 to 12,000 A/m. The high entropy alloy nanopowders have a broad application prospect in soft magnetic composites. [ABSTRACT FROM AUTHOR]

In this paper, a kind of zero valent FeNi alloy nano powder was coated on the surface of SrFe-MOF powder by a simple, efficient and pollution-free method, forming a core-shell type FeNi p @SrFe-MOF Magnetic powder (FSM). The FSM powder has a porous structure and a specific surface area of 9.16 ​m2/g. Under normal temperature and without changing the pH value of the wastewater, the FSM magnetic powder has an immediate and efficient removal effect on Congo Red (CR) dye wastewater. Furthermore, the powder has good cycling performance, with the CR removal rate remaining above 90% after five cycles. Also at room temperature and without changing the pH value of the wastewater, the FSM magnetic powder provides some immediate, efficient, and repeated use degradation of Cr(VI) wastewater. The FSM magnetic powder has good magnetic properties so that can be easily separated and recovered by magnetic field treatment, which solves the problem of efficient recovery of raw materials in wastewater treatment. FSM magnetic powder has broad application prospects for treating wastewater. In this paper, a kind of zero valent FeNi alloy nano powder was coated on the surface of SrFe-MOF powder by a simple, efficient and pollution-free method, forming a core-shell type FeNi p @SrFe-MOF Magnetic powder (FSM). Under normal temperature and without changing the pH value of the wastewater, the FSM magnetic powder has an immediate and efficient removal effect on Congo Red (CR) dye wastewater. Furthermore, the powder has good cycling performance, with the CR removal rate remaining above 90% after five cycles. Also at room temperature and without changing the pH value of the wastewater, the FSM magnetic powder provides some immediate, efficient, and repeated use degradation of Cr(VI) wastewater. The FSM magnetic powder has good magnetic properties so that can be easily separated and recovered by magnetic field treatment. [Display omitted] • FSM powder has an immediate and efficient removal effect on CR at room temperature and without changing the pH value of the wastewater. • FSM powder has some removal effect on Cr(VI) at room temperature and without changing the pH value of the wastewater. • FSM powder has good magnetic properties, which can be separated and recycled by magnetic field treatment. [ABSTRACT FROM AUTHOR]