Y 2 O 3 films with different microstructures were deposited through radio frequency magnetron sputtering. The optical properties and the antireflection effects of the cubic and the monoclinic Y 2 O 3 films on diamond substrates were investigated. Results showed that the cubic Y 2 O 3 film had denser and more uniform grains with larger grain size. The band gap energies of the cubic and the monoclinic Y 2 O 3 films were 5.79 and 5.88 eV, respectively. This finding was mainly attributed to the decrease in grain size from 30.1 nm to 20.6 nm. Meanwhile, the reflective indices of the cubic and the monoclinic films were 1.887 and 1.817, respectively. Furthermore, the monoclinic and the cubic Y 2 O 3 films that have the same thickness generated antireflection effects on diamond at the 8–12 μm long-wave infrared (LWIR) range. However, due to the lower reflective index of the monoclinic Y 2 O 3 film compared with that of the cubic Y 2 O 3 film, the maximum antireflection effects of the Y 2 O 3 films on diamond shifted to lower wavelengths. [ABSTRACT FROM AUTHOR]

Y 2 O 3 anti-reflection films were deposited on freestanding CVD diamond substrates by radio frequency magnetron sputtering. The thermal shock resistance and oxidation resistance of Y 2 O 3 /diamond/Y 2 O 3 samples at 727 °C and 800 °C in atmospheric air were investigated. No delamination of the Y 2 O 3 films occurred after thermal shock, thereby demonstrating extreme adhesion to freestanding diamond substrates. After thermal shock, Y atoms in the films were almost fully oxidized. Moreover, the majority of monoclinic phase in the Y 2 O 3 films transformed into cubic phase, crystallinity was enhanced, and the average grain size significantly increased. The maximum transmittance in the 8–12 μm long-wave IR range of the Y 2 O 3 /diamond/Y 2 O 3 samples increased from 81.3% ± 0.3% to 84.7% ± 0.2% and 83.6% ± 0.4%. These findings indicated that the Y 2 O 3 anti-reflection films displayed good resistance to thermal shock and provided sufficient protection for diamond substrates against elevated temperature oxidation. [ABSTRACT FROM AUTHOR]