The proven anti-neurodegenerative properties of caffeic acid in vivo are limited due to its poor solubility, which limits bioavailability. Therefore, caffeic acid delivery systems have been developed to improve caffeic acid solubility. Solid dispersions of caffeic acid and magnesium aluminometasilicate (Neusilin US2—Neu) were prepared using the ball milling and freeze-drying techniques. The solid dispersions of caffeic acid:Neu obtained by ball milling in a 1:1 mass ratio turned out to be the most effective. The identity of the studied system in comparison to the physical mixture was confirmed using the X-Ray Powder Diffractionand Fourier-transform infrared spectroscopy techniques. For caffeic acid with improved solubility, screening tests were carried out to assess its anti-neurodegenerative effect. The obtained results on the inhibition of acetylcholinesterase, butyrylcholinesterase, tyrosinase, and antioxidant potential provide evidence for improvement of caffeic acid's anti-neurodegenerative activity. As a result of in silico studies, we estimated which caffeic acid domains were involved in interactions with enzymes showing expression relevant to the neuroprotective activity. Importantly, the confirmed improvement in permeability of the soluble version of caffeic acid through membranes simulating the walls of the gastrointestinal tract and blood-brain barrier further strengthen the credibility of the results of in vivo anti-neurodegenerative screening tests. [ABSTRACT FROM AUTHOR]

The low bioaccessibility of hesperetin and piperine hampers their application as therapeutic agents. Piperine has the ability to improve the bioavailability of many compounds when co-administered. The aim of this paper was to prepare and characterize the amorphous dispersions of hesperetin and piperine, which could help to improve solubility and boost the bioavailability of both plant-origin active compounds. The amorphous systems were successfully obtained by means of ball milling, as confirmed by XRPD and DSC studies. What's more, the FT-IR-ATR study was used to investigate the presence of intermolecular interactions between the systems' components. Amorphization enhanced the dissolution rate as a supersaturation state was reached, as well as improving the apparent solubility of both compounds by 245-fold and 183-fold, respectively, for hesperetin and piperine. In the in vitro permeability studies simulating gastrointestinal tract and blood-brain barrier permeabilities, these increased by 775-fold and 257-fold for hesperetin, whereas they were 68-fold and 66-fold for piperine in the GIT and BBB PAMPA models, respectively. Enhanced solubility had an advantageous impact on antioxidant as well as anti-butyrylcholinesterase activities—the best system inhibited 90.62 ± 0.58% of DPPH radicals and 87.57 ± 1.02% butyrylcholinesterase activity. To sum up, amorphization considerably improved the dissolution rate, apparent solubility, permeability, and biological activities of hesperetin and piperine. [ABSTRACT FROM AUTHOR]

In this work, NiAl-xWC (x = 0 − 90 wt.% WC) intermetallic-based composites were successfully synthesized by mechanical alloying (MA) and a hot-pressing approach. As initial powders, a mixture of nickel, aluminum and tungsten carbide was used. The phase changes in analyzed systems after mechanical alloying and hot pressing were evaluated by an X-ray diffraction method. Scanning electron microscopy and hardness test examination were used for evaluating microstructure and properties for all fabricated systems from the initial powder to the final sinter stage. The basic sinter properties were evaluated to estimate their relative densities. Synthesized and fabricated NiAl-xWC composites showed an interesting relationship between the structure of the constituting phases, analyzed by planimetric and structural methods and sintering temperature. The analyzed relationship proves that the structural order reconstructed by sintering strongly depends on the initial formulation and its decomposition after MA processing. The results confirm that it is possible to obtain an intermetallic NiAl phase after 10 h of MA. For processed powder mixtures, the results showed that increased WC content intensifies fragmentation and structural disintegration. The final structure of the sinters fabricated in lower (800 °C) and higher temperature regimes (1100 °C), consisted of recrystallized NiAl and WC phases. The macro hardness of sinters obtained at 1100 °C increased from 409 HV (NiAl) to 1800 HV (NiAl + 90% WC). Obtained results reveal a new applicable perspective in the field of intermetallic-based composites and remain highly anticipated for possible application in severe-wear or high-temperature conditions. [ABSTRACT FROM AUTHOR]

Novel in situ Metal Matrix Nanocomposite (MMNC) materials based on titanium and boron, revealed their new properties in the nanoscale range. In situ nanocomposites, obtained through mechanical alloying and traditional powder metallurgy compaction and sintering, show obvious differences to their microstructural analogue. A unique microstructure connected with good mechanical properties reliant on the processing conditions favour the nanoscale range of results of the Ti-TiB in situ MMNC example. The data summarised in this work, support and extend the knowledge boundaries of the nanoscale size effect that influence not only the mechanical properties but also the studies on the cell viability and cytocompatibility. Prepared in the same bulk, in situ MMNC, based on titanium and boron, could be considered as a possible candidate for dental implants and other medical applications. The observed relations and research conclusions are transferable to the in situ MMNC material group. Aside from all the discussed relations, the increasing share of these composites in the ever-growing material markets, heavily depends on the attractiveness and a possible wider application of these composites as well as their operational simplicity presented in this work. [ABSTRACT FROM AUTHOR]

Magnesium and its alloys have been intensively investigated as potential bone implant materials. This paper discusses the influence of chemical composition on the microstructure, mechanical and corrosion properties of ultrafine grained Mg1Zn1Mn0.3Zr and Mg4Y5.5Dy0.5Zr alloys synthesized by the application of mechanical alloying and powder metallurgy. The hydroxyapatite or 45S5 Bioglass addition to Mg-based alloys decreases of grain sizes of the bulk material. The phase and microstructure analysis was carried out using X-ray diffraction, scanning electron microscopy and the properties were measured using hardness, nanoindentation and corrosion testing equipment. The properties of composites depend upon crystal structure, density, volume fraction, and the interface among the constituents, as well as upon the chemical composition and their final microstructure. The Mg1Zn1Mn0.3Zr composite surface improvement was achieved by electrolytic depositionof calcium phosphates from simulated body fluid electrolyte. The electrochemical test showed that the corrosion resistance of treated specimens was higher compared with the untreated samples in Ringer solution. The microstructure, composition andelectrolytic deposition of calcium phosphate coatings were characterized, and the corrosion properties of selected samples were also investigated. Ultrafine grained Mg-based biomaterials due to denser (Ca10(PO4)6O and (Mg(OH)2) surface layers, compared with untreated samples, possess unique surface properties and consequently are considered to be the future generation of biomaterials. [ABSTRACT FROM AUTHOR]

Ti(β) alloys have become an important class in the biomedical field due to low Young's modulus, excellent physical properties, and biocompatibility. However, their properties, like biocompatibility and, also, low wear resistance, can be still enhanced. To improve those properties, a composites approach can be applied. This research shows a new approach of the composite structure fabrication by powder metallurgy methods which for a stabile yttria-stabilized zirconia (YSZ) reinforcement phase could be obtained in the ultra-fine grain range beta-titanium matrix. In this work, the composites based on ultrafine-grain Ti-xMo (x = 23 wt%, 27 wt%, 35 wt%) alloys with addition 3 wt%, 5 wt% or 10 wt% YSZ, and 1 wt% Y2O3 were fabricated by the mechanical alloying and hot-pressing approach. Obtained composites were characterized in terms of their phase composition, microstructure, Young's modulus, hardness, surface free energy (SFE), and corrosion resistance. The structure of composites consists of phases based on Ti–Mo, Ti(α), and YSZ. The oxide (YSZ) powder tends to agglomerate during processing, which is revealed in composites based on Ti23Mo and Ti27Mo. However, composites based on Ti35Mo are characterized by a high degree of dispersibility and this influences significantly the hardness value of the composites obtained. Only in the case of composites based on Ti35Mo, the decrease in Young' Modulus is observed. All composites possess a hydrophilic surface property and good corrosion resistance. [ABSTRACT FROM AUTHOR]

Hydroxyapatite (HAp) is the most widely used material for bio coating. The functional layer can be produced by many methods, however, the most perspective by its utility, easy to scale up, and simplicity aspects remains a hydrothermal treatment approach. In this work, an HAp coating was produced by low-temperature hydrothermal treatment on the ultrafine-grain beta Ti-xMo (x = 23, 27, 35 wt.%) alloys. The proposed surface treatment procedure combines acid etching, alkaline treatment (AT), and finally hydrothermal treatment (HT). The uniqueness of the approach relies on the recognition of the influence of the molar concentration of NaOH (5 M, 7 M, 10 M, 12 M) during the alkaline treatment on the growth of hydroxyapatite crystals. Obtained and modified specimens were examined structurally and microstructurally at every stage of the process. The results show that the layer after AT consist of titanium oxide and phases based on sodium with various phase relations dependent on NaOH concentration and base composition. The AT in 7 M and 10 M enables to obtain the HAp layer, which can be characterized as the most developed in terms of thickness and porosity. Finally, selected coated samples were investigated in terms of surface wettability test managed in time relation, which for the results confirm high hydrophilicity of the surfaces. Conducted research shows that the low-temperature hydrothermal processing could be considered for a possible adaptation in the drug encapsulation and delivery systems. [ABSTRACT FROM AUTHOR]

In this study, the ultrafine-grained Ti23Zr25Nb-based composites with 45S5 Bioglass and Ag, Cu, or Zn additions were produced by application of the mechanical alloying technique. Additionally, the base Ti23Zr25Nb alloy was electrochemically modified in the two stages of processing: electrochemical etching in the solution of H3PO4 and HF followed by electrochemical deposition in Ca(NO3)2, (NH4)2HPO4, and HCl. The in vitro cytocompatibility studies were also done with comparison to the commercially pure titanium. The established cell lines of Normal Human Osteoblasts (NHost, CC-2538) and Human Periodontal Ligament Fibroblasts (HPdLF, CC-7049) were used. The culture was conducted among the tested materials. Ultrafine-grained titanium-based composites modified with 45S5 Bioglass and Ag, Cu, or Zn metals have higher biocompatibility than the reference material in the form of a microcrystalline Ti. Proliferation activity was at a stable level with contact with studied materials. In vitro evaluation research showed that the ultrafine-grained Ti23Zr25Nb-based composites with 45S5 Bioglass and Ag, Cu, or Zn additions, with a Young modulus below 50 GPa, can be further used in the biomedical field. [ABSTRACT FROM AUTHOR]

In this paper, binary β type Ti-23 at.% Mo alloys were obtained by arc melting as well as by mechanical alloying and powder metallurgical process with cold powder compaction and sintering or, interchangeably, hot pressing. The influence of the synthesis method on the microstructure and properties of bulk alloys were studied. The produced materials were characterized by an X-ray diffraction technique, scanning electron microscopy and chemical composition determination. Young's modulus was evaluated with nanoindentation testing method based on the Oliver and Pharr approach. The mechanically alloyed Ti-23 at.% Mo powders, after inductively hot-pressed at 800 °C for 5 min, allowed the formation of single Ti(β) phase alloy. In this case, Young's modulus and Vickers hardness were 127 GPa and 454 HV0.3, respectively. Among the examined materials, the porous (55%) single-phase scaffold showed the lowest indentation modulus (69.5 GPa). Analytical approach performed in this work focuses also on the surface properties. The estimation includes the corrosion resistance analyzed in the potentiodynamic test, and also some wettability properties as a contact angle, and surface free energy values measured in glycerol and diiodomethane testing fluids. Additionally, surface modification of processed material by micro-arc oxidation and electrophoretic deposition on the chosen samples was investigated. Proposed procedures led to the formation of apatite and fluorapatite layers, which influence both the corrosion resistance and surface wetting properties in comparison to unmodified samples. The realized research shows that a single-phase ultrafine-grained Ti-23 at.% Mo alloy for medical implant applications can be synthesized at a temperature lower than the transition point by the application of hot pressing of mechanically alloyed powders. The material processing, that includes starting powder preparation, bulk alloy transformation, and additional surface treatment functionalization, affect final properties by the obtained phase composition and internal structure. [ABSTRACT FROM AUTHOR]

In this work, mechanical alloying and electrical current-assisted sintering was adopted for in situ metal matrix composite material processing. Applied at the initial powder stage, mechanical alloying enables a homogeneous distribution of the starting elements in the proposed precursor powder blends. The accompanying precursor preparation and the structurally confirmed size reduction allow obtainment of a nanoscale range for the objects to be sintered. The nano precursors aggregated in the micro-sized particle objects, subjected to electrical current-assisted sintering, characterize the metal matrix composite sinters with high uniformity, proper densification, and compaction response, as well as maintaining a nanoscale whose occurrence was confirmed by the appearance of the highly dispersed reinforcement phase in the examined Ti-TiB material example. The structural analysis of the sinters confirms the metal matrix composite arrangement and provides an additional quantitive data overview for the comparison of the processing conditions. The mechanical alloying examined in this work and the electrical current-assisted sintering approach allow in situ metal matrix composite structures to create their properties by careful control of the processing steps. [ABSTRACT FROM AUTHOR]

Paper presents study on the hydrothermal treatment for hydroxyapatite layer formation on the different biodegradable Mg-substrates. The evaluation of corrosion resistance in Ringer's solution and contact angle measurements in glycerol were performed. Alloys and composites substrates obtained by mechanical alloying and powder metallurgy route are characterized by submicron range microstructure, which is responsible for further surface processing characteristic. Hydrothermal treatment in Ca-EDTA (ethylenediaminetetraacetic acid calcium disodium salt) led to formation of hydroxyapatite layers, which improves both the corrosion resistance and surface wetting properties compared to microcrystalline magnesium. [ABSTRACT FROM AUTHOR]