As-cast Mg–5.3Zn–0.6Ca (weight percent) alloy was indirectly extruded at 300 °C with different deformation rates (ram speeds of 0.1, 0.3, 0.5 mms − 1 ), and the microstructure, texture and mechanical properties of the as-extruded alloys were investigated in the current study. With the increase of deformation rates, the average size and volume fraction of dynamic recrystallized grains were remarkably increased. The basal fiber texture became weak in the as-extruded alloy with higher volume fraction of recrystallized grains, because most of the basal planes in these grains were tilted to extrusion direction about 30–40°. The higher deformation rate decreased the tensile yield stress due to the grain coarsening and basal texture weakening, while the elongation was improved, which was resulted from the enhanced work hardening rate. [ABSTRACT FROM AUTHOR]

The yield strength of the extruded Mg−9.9Y−3.7Zn (wt%) alloy at room temperature is remarkably increased from 240 MPa to 364 MPa using low-stain rolling. This significant improvement is ascribed to the combination of intensive basal texture, fine long-period stacking ordered phase particles and a high density of dislocations. The elongation of the rolled alloy increases as the strain of rolling increases, which is attributed to the homogenous distribution of fine long-period stacking ordered phases. [ABSTRACT FROM AUTHOR]