Search

Heat treatment is the critical step in achieving a refined microstructure and enhanced mechanical properties of TiAl-based alloys. This study investigated the influence of heat treatment temperature, cooling method, and heat treatment time on the microstructure and mechanical properties of an extruded powder metallurgy Ti-48Al alloy, and achieved the control of fully lamellar fine microstructures and the enhancement of performance through a simple heat treatment, rather than the traditional approach of homogenization followed by heat treatment. The results indicate that the heat treatment temperature determines the type of microstructure, while the cooling rate dictates the lamellar width. As the heat treatment temperature was increased from the two-phase region to the α single-phase region, the microstructure transitioned from duplex to near lamellar, and the alloy strength initially increased and then decreased, influenced by both the lamellar colony ratio and grain size. A rapid cooling rate (water quenching) induces a non-diffusive massive phase transformation, whereas a slow cooling rate (air cooling) gradually forms α2/γ lamellar colonies. Therefore, a suitable heat treatment regime for the powder metallurgy Ti-48Al alloy was determined to be 1340 °C/5 min/air cooling. The microstructure of the alloy was near lamellar, consisting of lamellar colonies approximately 50 μm and a small number of γ equiaxed grains of about 10 μm. Subsequently, the alloy exhibited a room temperature tensile strength of 784 MPa and a yield strength of 763 MPa, representing improvements of 17.0% and 38.7% over the extruded alloy, respectively. This research provides a reference for establishing a heat treatment process for powder metallurgy TiAl alloys. [ABSTRACT FROM AUTHOR]

TiAl-based alloy is an excellent high-temperature structural material, but poor hot workability has been the bottleneck hindering its development. In this study, we take into account the hot workability and mechanical properties of Ti-48Al alloy through microstructure adjustment. Powder metallurgy Ti-48Al alloy prepared by vacuum sintering is used as the raw material, which has a near-γ microstructure composed of equiaxed grains. Although the composition is simple, the alloy achieves high mechanical properties after forging with 75 % deformation. Controlling the forging temperature to 1300 °C can make the microstructure transform into a duplex structure composed of γ/α2 lamellar colonies and γ equiaxed grains. As-forged alloy has an ultimate tensile strength of 650 ± 17 MPa and a yield strength of 644 ± 16 MPa at room temperature. It still maintains high strength at high temperature, with ultimate tensile strength of 684 ± 19 MPa at 500 °C, 700 ± 19 MPa at 700 °C, and 320 ± 10 MPa at 900 °C. In addition, the alloy has good ductility with elongation of 58.2% due to dynamic recrystallization at 900 °C. • Mechanical property is significantly improved by forging with simple composition. • The alloy has ultrafine equiaxed grain of 2.45 µm and lamellar spacing of 20–50 nm. • Duplex microstructure without remnant lamellae forms in PM Ti-48Al alloy. • Ti-48Al alloy exhibits great plasticity of 58.2 % at 900 °C. [ABSTRACT FROM AUTHOR]

Cu Fe alloys with high iron content (Fe > 10 wt%) are a class of promising copper alloys with high strength and high conductivity. However, the strength and conductivity trade-off dilemma is a longstanding problem in the high iron content Cu Fe alloys owing to macro-segregation of iron particles and incomplete precipitation of solid solution iron atoms in the traditional casting process. We adopted a comprehensive strategy of designing the ultra-fine dual structures with fine copper grains and micro-nano iron particles, and adding phosphorus element to induce solid solution iron atoms precipitation to break through the above bottleneck. In this study, Cu 20Fe alloys with 0.05–1.0 wt% P were prepared through powder metallurgy process. The results showed that the addition of P promoted the precipitation of soluble Fe atoms, reduced oxygen content, and activated sintering. Ultimately, the strength and conductivity of cost-effective Cu 20Fe alloys were significantly improved. The annealed Cu 20Fe 0.1P alloys possess unprecedented comprehensive properties with 608 MPa tensile strength and 65.2% IACS electrical conductivity, which were 7.8% and 19.8% higher than the Cu 20Fe alloys, respectively. The annealed Cu 20Fe 1.0P alloys achieved 59.7% IACS electrical conductivity, increased by 10% compared to Cu 20Fe alloys. The results broke the conventional understanding that increasing P content deteriorated material properties. The influence of P on the microstructure and properties of powder metallurgy Cu 20Fe alloys was investigated in detail. These findings provide new insight into overcoming the dilemma of the inverted relationship between the strength and conductivity of copper alloys. • Simultaneous enhancement of the mechanical and electrical properties of Cu 20Fe alloys by introducing phosphorus. • The Cu 20Fe 0.1P alloys possess unprecedented comprehensive properties and property-costs. • The influence of P on the microstructure and properties of powder metallurgy Cu 20Fe alloys was investigated in detail. [ABSTRACT FROM AUTHOR]

In this paper, the microstructural evolution, precipitation behavior and mechanical properties of 2195 Al-Li alloys prepared by powder metallurgy (PM) combined with hot extrusion were investigated systematically. The results show that the deformation of PM 2195 Al-Li alloys during hot extrusion is dominated by the coupling of dynamic recovery with continuous dynamic recrystallization. The homogeneously distributed needle-like T 1 phase is precipitated in the matrix after T6 treatment. The T6-treated sample exhibits a perfect combination of strength and ductility, that is, ultimate tensile strength of 662 MPa, yield strength of 617 MPa and uniform elongation of 6.6 %. The strengthening of heat-treated alloys originates from densification, work hardening, grain refinement and precipitation strengthening. It is noted that the precipitation strengthening of T 1 phase is the dominant mechanism. Therefore, this work should suggest a strategy for developing novel Al-Li alloys with excellent mechanical properties. • The 2195 Al-Li alloys were successfully prepared by powder metallurgy and hot extrusion. • The tensile strength, yield strength and elongation of the 2195 Al-Li alloy were 662 MPa, 617 MPa and 6.6 %, respectively. • Mechanical properties of the alloy were enhanced by densification, work hardening, grain refinement and precipitation. • The precipitation strengthening of T 1 phase is the dominant mechanism. [ABSTRACT FROM AUTHOR]

Simultaneous improvement of both the strength and electrical conductivity of Cu–Fe alloys (CFAs) through the conventional casting method is an extremely challenging task. In this study, an attempt was made to overcome this issue via preparing CFAs with ultrafine alloy powders embedded with nano Fe particles. Ultrafine CFA powders with various Fe contents ranging from 5 to 50 wt.% were synthesized by a novel rapid solidification route, namely, gas–water combined atomization (GWA) process. The alloy powders prepared via GWA were then processed by pressureless sintering, hot rolling, annealing, and cold rolling. The microstructure evolution, mechanical properties, and electrical conductivity of CFAs were comprehensively investigated. The average size of Cu grain and Fe particles in all sintered CFAs was smaller than 3 and 2 μm, respectively. The grains of sintered CFAs were obviously refined by the Fe particles, and the addition of Fe inhibited the formation of Cu twins. After rolling, the Fe particles elongated and became fibrous along the rolling direction. The degree of formation of fibrous Fe enhanced with the increase of Fe content. Cold-rolled CFAs with 5–50 wt% Fe exhibited the tensile strength of 560–1250 MPa and conductivity of 33–65% IACS, indicating that CFAs in this study achieved superior mechanical and electrical properties. The microstructure evolution and strengthening mechanisms of CFAs were described. These findings can provide new insights into the powder metallurgy manufacturing of high-performance CFAs. • Ultrafine CFA powders were prepared by gas-water combined atomization. • The average size of Fe particles and grains of sintered CFAs was 2–3 μm. • Cold-rolled CFAs achieved superior mechanical and electrical properties. [ABSTRACT FROM AUTHOR]

Powder metallurgy Cu-30Fe alloy was prepared by mechanical alloying, pressureless sintering, and rolling processes. The alloy microstructure and physical properties affected by rolling were studied. The Fe particles were small and uniformly distributed in the Cu matrix. The average Fe particle size in the sintered state was 1 µm, and particles had subspherical or irregular shapes. The Fe particles became elongated, tadpole-shaped, and spindle-shaped as a result of rolling. At the same time, the Cu grains were elongated and refined, while the Cu grains near the Fe particles were finer as a result of the coordinated deformation of the soft Cu and hard Fe phases. After annealing at 400 °C, the cold-rolled Cu-30Fe alloy had 620 MPa tensile strength, 10% elongation, and 50% IACS electrical conductivity, achieving a good combination of mechanical and functional properties. The coordinated deformation behavior and grain refinement mechanisms of both Cu and Fe phases due to rolling were described, along with the microstructure and physical properties evolution. • Cu-30Fe alloys with Fe particles were fabricated by powder metallurgy and rolling. • Grain refinement mechanisms of Cu and Fe phases due to rolling were described. • Microstructure and physical properties of Cu-30Fe alloys were studied. • Cu-30Fe has 620 MPa tensile strength, 10% elongation, 50%IACS electrical conductivity. [ABSTRACT FROM AUTHOR]