Search

This paper investigated the fracture toughness and enhancement mechanism for each component in bamboo-based composites at the cellular level. In situ characterization techniques identified the fracture behaviors of bamboo-based composites in three-point bending tests, and scanning electron microscope (SEM) further visualized the crack propagation of the fracture surface. In addition, the improvement mechanism of bamboo-based composites was illustrated by mechanical properties at the cellular level assisted with nanoindentation tests. Our in situ test results showed that the bamboo-based composites exhibited a longer deformation and higher bending load compared with bamboo. The fracture was non-catastrophic, and crack propagated in a tortuous manner in bamboo-based composites. Microstructural analysis revealed that phenol-formaldehyde (PF) resin pulled out and middle lamella (ML) breaking rather than transverse transwall fracturing occurred in parenchymal cells. The higher density of fibers in the bamboo-based composites triggered massive interfacial delamination in the middle lamella (ML), which was a weak mechanical interface. Furthermore, indented modulus and hardness illustrated that phenol-formaldehyde (PF) resin improved the mechanical strength of cell walls, especially parenchymal cells. The crosslinks of PF resin with the cell walls and massive fibers were the primary mechanisms responsible for the fracture toughness of bamboo-based composites, which could be helpful for advanced composites. [ABSTRACT FROM AUTHOR]

This study aims to quantitatively analyze the three-dimensional microstructure of ultra-thin HDF paving boards and molding boards, in order to explore the modeling methods of HDF and attempt to predict its mechanical properties more accurately through theoretical and simulation analyses. In this study, non-destructive analysis of the internal microstructure was conducted using computed tomography (CT) imaging technology. The characteristics of microstructural evolution during the hot compression molding process were explored, and all analyzed data were utilized for 3D reconstruction and simulation model construction. Ultra-thin fiberboards with different fiber ratios were modeled through volume compression and experimentally simulated in tension. The results were compared with experimentally determined results for verification purposes. Additionally, differences in surface roughness, water absorption, and expansion of ultra-thin fiberboards with varying fiber ratios were analyzed. The findings indicate that different fiber ratios have a significant impact on the mechanical properties of ultra-thin fiberboards; tensile strength increases with an increase in medium-length fibers content when fibers are pulled or split, highlighting the key role played by the strength of the fibers themselves. Furthermore, it was observed that surface roughness and water-absorbing expansion rate are lower when a higher proportion of fine fibers is present. The results from this study hold great significance for gaining a deeper understanding of the composition, structure, and properties of ultra-thin fiberboards as well as exploring modeling methods for high-density fiberboards. They also provide guidance for optimizing material formulations and preparation processes while improving performance and quality standards for poplar-ultra-thin fiberboards. • We quantitatively analysed the three-dimensional microstructure of ultra-thin fibreboard paving slabs and moulded panels. • We explored the modelling method of high-density fibreboard and obtained a model of high-density fibreboard with a volume fraction of 90%. • We explored the effects of different fibre ratios on the mechanical properties of ultra-thin fibreboards. [ABSTRACT FROM AUTHOR]

• Successfully joined magnesium and aluminum dissimilar metals by nanosecond pulsed laser welding technology. • The laser power has a significant effect on the weld appearance, interface organization, fracture morphology and mechanical properties. • The heat transfer mechanism of the molten pool is described, and two paths of heat transfer are proposed. • At a laser power of 25 W, the maximum tensile force of the joint is the largest, which is 76.5 N. • The temperature field during the welding process was simulated. AZ31B magnesium alloy and 6061 aluminum alloy of 0.2 mm thickness were joined by nanosecond pulsed laser welding technology, and the effects of nanosecond pulsed laser power on the formation of weld seam, interface microstructure and mechanical properties were investigated, and numerical simulation of the temperature field during the welding process was carried out. The results show that when the laser power is 50 W, more defects such as cracks, pores and sags appeared in the joints due to the high heat input, and these defects resulted in a smaller effective joint area between the metals, which is very unfavorable to the strength of the joints. As the laser power decreases, at a laser power of 25 W, fewer defects are exhibited and the effective joint area becomes larger. As the laser power continues to decrease, the low heat input makes metal melting and joining very difficult. At low laser power, the Mg element intrudes backwards into the aluminum, causing the joint boundary interface to take on a reverse "V" shape. According to the results of the tensile shear experiments, the maximum tensile force of the joint was the highest at a laser power of 25 W, which reached 76.5 N. In addition, it was observed that the effective joint area, the number of oxides and their inclusions, and the degree of angular deformation had a very important effect on the mechanical properties of the joints. The results of temperature field numerical simulation experiments show that the heat is accumulated from outside to inside during the laser scanning process, and whether the temperature in the center of the molten pool reaches the melting point of the alloy can be used as an important basis for analyzing the degree of welding. [ABSTRACT FROM AUTHOR]

• The magnesium alloy and 304 stainless steel were successfully joined via nanosecond pulsed laser welding. • Highest tensile shear force of 298.7 N was obtained at the speed of 30 mm/s. • Three fracture modes produced at various welding speeds were clarified. • The welding temperature field of magnesium/steel joint was simulated. Nanosecond pulse laser welding was performed on AZ31B magnesium alloy and 304 stainless steel to investigate the impact of welding speed on the joining process. The temperature field of the magnesium/steel laser welding process was simulated using COMSOL software. The findings revealed that a welding speed of 10 mm/s resulted in significant spattering and larger porosity defects in the joint due to excessive heat input. However, when the welding speed was increased to 30 mm/s, these defects disappeared, and the porosity decreased to a minimum, leading to an increased bonding area at the interface. As the speed increased, the heat input decreased, making it more challenging for the porosity to escape from the molten pool and resulting in the formation of larger pores. The shear force test results indicated that the highest shear force was 298.7 N at a welding speed of 30 mm/s. The reduction in porosity and greater penetration depth of the magnesium alloy contributed to the desired mechanical performance. Additionally, the fracture modes were classified as button pullout failure (BPF), base material tearing failure (BTF), and interface failure (IF). The outermost weld seam served as the initial fracture path for both BPF and BTF modes, with BTF ultimately fracturing in the steel base material during tearing. Oxide inclusions, porosity, and the angle of distortion contributed to the fracture path of IF. [ABSTRACT FROM AUTHOR]