Search

Abstract: This study aims at developing an effective method to modify hydrophobic polyvinylidene fluoride (PVDF) membranes for membrane distillation (MD) which is tolerant to salty feed solution containing mineral oil. A novel approach was explored to obtain a highly hydrophilic membrane surface via plasma induced grafting of polyethylene glycol (PEG) and subsequent TiO2 particles deposition onto the membrane surface. The mechanism of oil affinity onto a membrane surface was quantitatively investigated by the extended Derjaguin–Landau–Verwey–Overbeek (XDLVO) theory. A series of characterizations were conducted for the virgin and modified membranes. Membrane distillation tests for synthetic seawater containing 0.01wt% of mineral oil were also performed to investigate the influences of membrane hydrophobicity, membrane surface structure, pH value of the feed solution and hydrodynamic conditions on oil fouling behavior. The SEM and FTIR measurements confirmed the presence of PEG and TiO2 particles on the PVDF membrane substrate. The hydrophilically modified PVDF-PT membrane exhibits a positive interfacial free energy with oil in the feed, indicating the TiO2 deposition effectively improve the anti-fouling property of PVDF-P membrane and PVDF membrane. It was also found that the PVDF-PT membrane presents a stable water flux over 24h of operation without fouling and wetting due to combined effects of enhanced surface hydrophilicity and reduced membrane pore sizes. In addition, the pH value of the feed solution plays an important role in oil fouling. More severe fouling can be observed at the pH which made the membrane surface and oil droplets carry opposite charges. Moreover, a higher flow velocity enhances the shear force exerted on the oil droplets, thus leading to less oil present on the membrane surface and less oil fouling of the membrane. [Copyright &y& Elsevier]

Hydrophobic membranes suffer from wetting and scaling when treating hypersaline brine using membrane distillation (MD). Thus omniphobic membranes with re-entrant surfaces have been developed by diverse modifications to enhance anti-wetting/scaling properties. However, those post-modifications usually sacrifice membrane permeability in spite of improved stability. In this work, omniphobic membranes were fabricated by decorating polyvinylidene fluoride (PVDF) nanofibrous membranes with different silica nanoparticles (SiNPs) followed by fluorination. Compared to unmodified nanofibrous and commercial PVDF membranes, both smaller SiNPs coated membrane #P-Min and larger SiNPs coated membrane #P-Max can perfectly sustain liquids with low surface tensions on their surfaces without wetting. In contrast to #P-Max with an oil contact angle of 136 ± 1°, #P-Min exhibited better oleophobicity with an oil contact angle of 152 ± 1°. In addition, the rigidity of their omniphobic properties was confirmed by testing in harsh conditions. Moreover, #P-Min successfully overcame the trade-off relation between membrane permeability and rejection with an enhanced MD flux due to more effective water evaporation area on membrane surface and a higher membrane porosity. While #P-Max was wetted by a hypersaline feed solution composed of 25 wt% NaCl, #P-Min could maintain a stable flux of 15 L m−2h−1 in a continuous 7-h MD operation, which proved its excellent performance for brine treatment. Furthermore, #P-Min exhibited less scaling tendency when feed was a saturated gypsum solution. Compared to #P-Max , the better anti-scaling properties of #P-Min should be due to its higher surface energy barrier, better slippery property and less solid-liquid contact area, which effectively impede crystal nucleation and attachment. Image 1 • Effects of nano-scaled roughness on membrane omniphobicity were studied. • As-prepared omniphobic membranes were stable under harsh conditions. • Omniphobic membrane coated with smaller NPs exhibited better performance. • It should be due to high surface energy barrier, slippery property and less solid-liquid contact area. [ABSTRACT FROM AUTHOR]