Critical current (Ic) values of 1384 A/12 mm, corresponding to a critical current density of 12.47 MA cm−2 and a pinning force of 374 GN m−3, have been achieved at 30 K, 3 T in the orientation of field parallel to the c axis (B ∥ c) in (Gd, Y)BaCuO tapes with 15 mol% Zr addition made by metal organic chemical vapor deposition (MOCVD). These tapes show pinning force levels as high as 453 GN m−3 at 30 K. An analysis of the properties of 24–28 (Gd, Y)BaCuO tapes with 15 mol% Zr addition showed a lack of correlation between their critical currents at 30 K, 3 T (B ∥ c) and Ic values both at 77 K, zero field and at 77 K, 1 T (B ∥ c). However, a strong correlation was found between the critical currents at 30 K, 3 T and at 77 K, 3 T (B ∥ c). It has also been discovered that the minimum critical current (Ic, min) value at 77 K, 3 T has no influence on the Ic, min value at 30 K, 3 T, and it in turn depends on the ratio of the Ic values in the orientations of field parallel and perpendicular to the c axis at 77 K, 3 T. [ABSTRACT FROM AUTHOR]

The critical current and structural properties of (Gd,Y)BaCuO tapes made by metal organic chemical vapor deposition (MOCVD) with Zr addition levels up to 30 at.% have been investigated. The reduction in critical current beyond the previously optimized Zr addition level of 7.5 at.% was found to be due to structural deterioration of the (Gd,Y)Ba2Cu3Ox film. By a modified MOCVD process, enhanced critical current densities have been achieved with high levels of Zr addition, including 3.83 MA cm-2 in 15 at.% Zr-added 1.1 µm thick film at 77 K in zero magnetic field. Critical currents as high as 1072 A/12 mm have been reached in (Gd,Y)BaCuO tapes with 15 at.% Zr addition at 30 K in a field of 3 T applied perpendicular to the tape, corresponding to a pinning force value of 268 GN m-3. The enhanced critical currents achievable with a high density of nanoscale defects by employing high levels of second-phase additions enable the performance targets needed for the use of HTS tapes in coil applications involving high magnetic fields at temperatures below 50 K to be met. [ABSTRACT FROM AUTHOR]