We report on the growth of In0.30Ga0.70As channel high electron mobility transistor (HEMT) epi-layers on a 200-mm Si substrate by metal-organic-chemical-vapor-deposition. The HEMT layers were grown on the Si substrate by using a ~3- \mu \textm thick epitaxial buffer composing of a Ge layer, a GaAs layer, and a compositionally graded and strain relaxed InAlAs layer. The optimized epitaxy has a threading dislocation density of less than 2 \times 10^7 cm−2 and a root mean square surface roughness of ~6.7 nm. The device active layers include a \delta -doped InAlAs bottom barrier, a ~15-nm thick InGaAs channel, a ~8-nm InGaP top barrier layer and a heavily doped InGaAs contact layer. MOSHEMTs with channel length down to 130 nm were fabricated. The devices achieve a peak transconductance of \sim 450 ~\mu \textS/ \mu \textm at V D of 0.5 V. The peak effective mobility ( \mu \text {eff} ) in a device with a channel length of 20 \mu \textm device channel was ~3700 cm2/ \textV \cdot \texts . [ABSTRACT FROM AUTHOR]

We report on the growth of an In0.30Ga0.70As channel high-electron mobility transistor (HEMT) on a 200 mm silicon wafer by metal organic vapor phase epitaxy. By using a 3 µm thick buffer comprising a Ge layer, a GaAs layer and an In- AlAs compositionally graded strain relaxing buffer, we achieve threading dislocation density of (1.0 ± 0.3) × 107 cm-2 with a surface roughness of 10 nm RMS. No phase separation was observed during the InAlAs compositionally graded buffer layer growth. 1.4 µm long channel length transistors are fabricated from the wafer with IDS of 70 µA/µm and gm of above 60 µS/µm, demonstrating the high quality of the grown materials. [ABSTRACT FROM AUTHOR]