Spin polarized photocathodes are key to the future operation of electron accelerators such as the ones at Thomas Jefferson National Accelerator Facility and Brookhaven National Laboratory. Currently, these photocathodes come in short supply due to limited production by molecular beam epitaxy. By developing a process to implement similar structures using metal organic chemical vapor deposition, the availability of these devices can be increased. In this paper, we detail the implementation of recent photocathode advancements via metal organic chemical vapor deposition process and show an improvement in both polarization and quantum efficiency of our devices compared to those fabricated via molecular beam epitaxy, with devices reaching 82% polarization and 2.9% quantum efficiency. [ABSTRACT FROM AUTHOR]

Intermediate band solar cells promise improved efficiencies beyond the Shockley-Queisser limit by utilizing an intermediate band formed within the bandgap of a single junction solar cell. InP quantum dots (QDs) in an In0.49Ga0.51P host are a promising material system for this application, but two-step photon absorption has not yet been demonstrated. InP QDs were grown via metalorganic chemical vapor deposition, and a density, a diameter, and a height of 0.7 × 1010 cm−2, 56 ± 10 nm, and 18 ± 2.8 nm, respectively, were achieved. Time-resolved photoluminescence measurements show a long carrier lifetime of 240 ns, indicating a type-II band alignment of these InP quantum dots. Several n-i-p In0.49Ga0.51P solar cells were grown with both 3 and 5 layers of InP QDs in the i-region. While the solar cells showed an overall loss in short circuit current compared to reference cells due to emitter degradation, a sub-bandgap enhancement of 0.11 mA/cm2 was clearly observed, due to absorption and collection from the InP QDs. Finally, two-step photon absorption experiments have shown unambiguous photocurrent generation involving an intermediate band within the bandgap at temperatures up to 250 K. [ABSTRACT FROM AUTHOR]