Search

Abstract: CZ doped by nickel oxide with different loadings was prepared through a co-precipitation and supercritical dried method and the corresponding Pd-only TWCs were prepared and characterized. The results demonstrate that Pd/CZNi(3%) catalyst exhibits the best catalytic activity and the widest operation window before and after aging, compared with that of other catalysts. Moreover, the introduction of nickel oxide with 3% loading increases the average pore diameter and broadens the range of pore size distribution of sample, which is propitious to the formation of accumulative pore favoring the adsorption/desorption of reaction species. The introduction of nickel oxide with suitable loading (3%) promotes the thermal stability of CZ corresponding to the better surface composition and more concentration of Ce3+ or oxygen vacancy. Furthermore, the introduction of nickel oxide with 3% loading exhibits the best DOSC compared with other content doping, possibly due to the better structure and better surface composition and better thermal stability of CZNi(3%). [Copyright &y& Elsevier]

Abstract: CeO2-ZrO2 doped by nickel oxide (CZN) with different method and Pd-only three-way catalysts (Pd/CZN) were prepared and characterized. The catalyst prepared by co-precipitation and supercritical drying process (Pd/CZN-s) exhibits the best catalytic activity and the widest operation working window before and after aging. Compared with other samples, CZN-s shows the formation of more homogeneous ternary solid solution with the smallest lattice parameter and crystallite size. Moreover, CZN-s maintains the high thermal and structural stability with higher surface area and larger pore volume after aging. Pd/CZN-s exhibits higher relative concentration of Ce3+ associated with the formation of more oxygen vacancies before and after aging, confirmed by X-ray photoelectron spectroscopy and Raman results. The more concentration of Ce3+ or oxygen vacancies leads to the enhancement of oxygen storage complete capacity of CZN-s. Moreover, the higher the oxygen storage capacity, the wider the working ranges of air/fuel variations. [Copyright &y& Elsevier]

Abstract: Ce0.67Zr0.33O2 doped with iron oxide was prepared and the corresponding Pd-only three-way catalysts were examined and characterized. Pd/CZFe(1%) catalyst exhibits the best catalytic performance for CO, HC, NO and NO2 elimination and the widest operation window. The doping of iron oxide with 1% loading suggests the formation of more homogeneous Ce–Zr–Fe–O ternary solid solution, which seems to facilitate the reduction of Ce4+ →Ce3+ or the formation of oxygen vacancy and to promote the interaction between Ce–Zr and Fe. Moreover, the Ce redox behaviour for surface reduction suggests depending not only on the formation of homogeneous Ce–Zr–Fe–O but also on the surface property of the sample. The increase in the concentration of oxygen vacancies under all atmospheres for CZFe(1%) sample also results in the enhancement of oxygen storage complete capacity. [Copyright &y& Elsevier]

Abstract: The promotional effect of cobalt oxide on the catalytic performance and the physicochemical properties of Pd only three-way catalysts and Ce0.67Zr0.33O2 mixed oxides (CZ) prepared by co-precipitation and impregnation methods have been investigated. It is worthwhile to note that the role of Co significantly depends on the method of Co doping in the CZ. The introduction of cobalt oxide by co-precipitation exhibits significant influence on the catalytic activity of Pd only three-way catalyst with enhancing textural and structural properties, compared to the introduction of cobalt oxide by impregnation method. Furthermore, CZ doped with cobalt oxide by co-precipitation results in the formation of more homogeneous ternary solid solution, which promotes the metal–support interaction between CZ and cobalt metal and improves oxygen storage capacity (OSC) of samples. It also proves that the textural and structural properties of supports can affect the reducibility and oxygen storage capacity of samples at low temperature. [Copyright &y& Elsevier]

Abstract: Ce0.67Zr0.33O2 (CZ) doped by nickel oxide with different content and the corresponding Pd-only three-way catalysts before and after aging has been prepared and characterized. The investigations show that CZ doped with nickel oxide obviously results in more active fresh catalysts with enhanced textural properties, but suffers from a net loss of activity after aging. The introduction of Ni promotes the reducibility of samples, causing the enhancement of oxygen storage capacity (OSC) of fresh samples. CZNi(3%) exhibits better textural and structural properties because of the formation of more homogeneous Ce–Zr–Ni–O ternary solid solution, which promotes the interaction between Ce–Zr and Ni. However, the thermal aging leads to a loss of surface area and a significant decrease of the reducibility and OSC, except for CZNi(3%). Only Pd/CZNi(3%) represents better catalytic activity after aging. It reveals that the catalytic behavior of these bimetallic systems is strongly affected by the nature of support. [Copyright &y& Elsevier]

Abstract: CeO2–ZrO2–Al2O3 (CZA) mixed oxides were synthesized using sol–gel and supercritical drying methods, and their physicochemical properties were characterized by BET surface area (BET), X-ray diffraction (XRD), H2-temperature-programmed reduction (H2-TPR) and O2-temperature-programmed desorption (O2-TPD) techniques. The catalytic performances of Pd/CZA catalysts with different thermal treatment were also investigated. The results indicate that catalytic activities are affected by thermal treatment of support or catalyst and Pd/CZA catalysts exhibit good thermal stability. H2-TPR results show that the effect of thermal treatment on the dispersion state of PdO is different between catalyst and support after calcination. However, O2-TPD results show that the influence of thermal treatment on the desorption performance of oxygen is similar in both cases. Desorption of surface oxygen is closely related to surface area of the support. During the calcination of the supports or the catalysts at high temperature, the surface oxygen desorption capacity and the mobility of lattice oxygen decrease due to the sintering of supports, which is harmful to the dispersion of active species, corresponding to the decrease of three-way catalytic activities. [Copyright &y& Elsevier]

Abstract: Four types of Ce0.67Zr0.33O2 (CZCP, CZH, CZHP and CZM) mixed oxides as supports were prepared by coprecipitation, hydrothermal, homogeneous precipitation and microemulsion methods, respectively. The results show that both the preparation methods and the aging procedures have significant influences on the physicochemical properties of Ce0.67Zr0.33O2 mixed oxides. All these fresh Ce0.67Zr0.33O2 samples develop mesopore structure, especially that, CZCP obtains the largest diameter (20.87nm) and volume (0.455cm3/g). The XRD results indicate that fresh CZHP and CZCP samples contain cubic and tetragonal phases, while only cubic solid solution is found in fresh CZH and CZM samples, which show better low-temperature reducibility. Moreover, higher oxygen storage capacity complete (OSCC) values and faster O2 uptake are observed in CZH and CZM samples compared with those of fresh CZCP and CZHP. After calcination at 1100°C, it is found that the OSCC values and the kinetics of the O2 uptake for CZM and CZHP samples are deteriorated due to the coexistence of cubic and tetragonal phases as well as strong sintering of samples. On the contrary, the aged CZCP and CZH samples keep satisfactory low-temperature reducibility and oxygen storage capacity. For fresh catalysts, the pore-size distribution of mixed oxides seems to be important for catalytic activities. In contrast, for aged catalysts, their activities are related to both the redox properties and the textural properties of aged mixed oxides. Therefore, the Pd-only three-way catalyst supported on the CZCP exhibits the most promising amplified amplitude of stoichiometric window. [Copyright &y& Elsevier]