Electromagnetic welding, also referred to as magnetic pulse welding, is a solid-state welding method utilized for joining two distinct materials through high velocity impact. The direct fusion of stainless steel with titanium poses various difficulties owing to the absence of metallurgical compatibility and the occurrence of brittle intermetallic compounds such as FeTi and CrTi. To tackle these challenges, a sustainable, low heat input method like impact welding was applied to address the metallurgical compatibility of the two metals. In this study, a new technique involving aluminum foil, silver foil, and nitinol powder as intermediary materials was investigated to establish a fresh bimetallic structure between Ti-SS304L. Thorough analysis of microstructures, interface formations, and reactions was conducted using scanning electron microscopy and X-ray diffraction. The outcomes showcased successful prevention of intermetallic phase formation through the incorporation of these intermediary materials. Microhardness measurements indicated the absence of brittle FeTi and CrTi phases at the welding interface. Additionally, the weld interface was observed to be situated amid two intermetallic layers at the Ti-SS304L interface, ensuring resistance against corrosion. This inventive method not only averted the creation of harmful intermetallic compounds but also bolstered the overall strength and corrosion resilience of the joint between titanium and stainless steel. The micro hardness obtained at Ti-SS304L interface is 305 Hv and also improved 20% at interface of interlayer materials. [ABSTRACT FROM AUTHOR]

The composite was made using the stir cast manufacturing method. Many parameters, like stirring speed, stirring time, ZrO2% reinforcement, and cast temperature, are evaluated in a Taguchi experimental design to see how they affected the composite properties. In terms of composite properties, ZrO2% reinforcement and the stir speed have the most significant impact. There were 25.02% gains in ultimate tensile strength and hardness, as well as a decrease in composite wear loss, when the optimal stir casting parameters were used compared to the initial stir casting settings. To get insight into the process and the qualities of the composite, the hot-pressing parameters were studied. Pressure, followed by temperature, is the most critical factor in determining the properties of composites. When a hot-pressing setting was determined to reduce the wear loss by a significant 39.3%, it was deemed perfect by the superranking concept. Under ideal conditions, hot-pressing procedures reduced wear loss by 40.8% while boosting ultimate tensile strength and hardness by 19.83% and 9.6%, respectively. The resulting microstructures and worn surface morphologies from stir casting and hot pressing show vastly different properties. [ABSTRACT FROM AUTHOR]