Search

Objective: The use of calcium silicate-based cements has greatly increased in the past decade. This study compared coronal discolouration caused by white mineral trioxide aggregate (MTA), TheraCal (TC), calcium enriched mixture (CEM), and Biodentine (BD) on bovine enamel-dentin block. Methods: In this in vitro, experimental study, enamel-dentin blocks (7x7x3.5 mm) were cut out of 60 extracted sound bovine central incisors. A cavity (2.5 mm diameter and 1 mm depth) was created at the center of each block with 1 mm distance from the labial surface. The blocks were randomly divided into four experimental groups (n=12) of MTA, CEM, BD, and TC and two groups of positive (blood) and negative (empty) controls. After filling cavities with experimental materials, the surfaces of the materials were covered with composite resin. The colour parameters were measured using a spectrophotometer, before (T0) and 1 week (T1), 1 month (T2), and 6 months (T3) after the application of the materials. The data was analysed using repeated measures ANOVA and the Kruskal-Wallis test. Results: At 1 week and 1 month, a significant difference in ΔE was noted in the control groups compared to the experimental groups (P<0.001). The difference among the four cements was not significant (P=0.06) at 1 week but it was significant at 1 month. TC showed greater ΔE whereas BD showed lower ΔE in the six-month period (P<0.001). Colour change was significant over time in the MTA and TC groups (P<0.05). Conclusion: TheraCal caused greater discolouration in the bovine tooth blocks after 6 months, which may make it inappropriate for application in the aesthetic zone. [ABSTRACT FROM AUTHOR]

Objective(s): Biocompatibility of dental biomaterials plays a critical role in regeneration of dental stem cells. The aim of present study was to evaluate the effects of novel biomaterials of TheraCal-LC (TheraCal; Bisco), Angelus mineral trioxide aggregate (MTA; Angelus), calcium-enriched mixture (CEM; BioniqueDent), and Biodentine (Septodont) on viability of human dental pulp stem cells (hDPSCs). Moreover, the recruitment of dental pulp stem cells is a prerequisite for regeneration of damaged dentin. Therefore, in this study the effects of mentioned biomaterials on migration of hDPSCs and the secretion of some chemoattractive molecules by these cells were examined. Materials and Methods: The cell viability of hDPSCs was assessed using MTT assay. Transwell migration assay was used to determine cell migration ability. The cytokine secretion was evaluated using enzyme-linked immunosorbent assay. Results: The biomaterials of MTA, CEM, and Biodentine at different dilutions had no cytotoxic effects on hDPSCs at different time points; however, non-diluted extract of TheraCal showed toxic effects after 24, 48, and 72 hr. Meanwhile, the highest cell migration was observed in the presence of CEM and Biodentine (PConclusion: The biological compatibility associated with CEM and Biodentine indicates promising applications in the field of vital pulp therapy.

Vital pulp therapy (VPT) and direct pulp capping (DPC) are procedures regularly performed in dogs for the management of acute tooth fractures and as part of management for traumatic malocclusions. The purpose of this review is to apply an evidence-based medicine approach to systematically review and evaluate the scientific literature evaluating the efficacy of mineral trioxide aggregate (MTA) to other commercially available materials used for VPT in the permanent teeth of dogs. The 9 studies meeting inclusion criteria were reviewed and each studies evidence was classified using a grading system modified from the Oxford Centre for Evidence-Based Medicine. For the studies meeting inclusion criteria, MTA consistently performed as well or better than other commercially available products in terms of calcific barrier formation and biocompatibility. This review found a lack of consistency between the studies making a direct comparison of the results unreliable. Future studies would benefit from the implementation of a standard scoring system for histology, equivalent and longer study duration times and the correlation of histological and radiographic data. [ABSTRACT FROM AUTHOR]

Objective(s): Biocompatibility of dental biomaterials plays a critical role in regeneration of dental stem cells. The aim of present study was to evaluate the effects of novel biomaterials of TheraCal- LC (TheraCal; Bisco), Angelus mineral trioxide aggregate (MTA; Angelus), calcium-enriched mixture (CEM; BioniqueDent), and Biodentine (Septodont) on viability of human dental pulp stem cells (hDPSCs). Moreover, the recruitment of dental pulp stem cells is a prerequisite for regeneration of damaged dentin. Therefore, in this study the effects of mentioned biomaterials on migration of hDPSCs and the secretion of some chemoattractive molecules by these cells were examined. Materials and Methods: The cell viability of hDPSCs was assessed using MTT assay. Transwell migration assay was used to determine cell migration ability. The cytokine secretion was evaluated using enzymelinked immunosorbent assay. Results: The biomaterials of MTA, CEM, and Biodentine at different dilutions had no cytotoxic effects on hDPSCs at different time points; however, non-diluted extract of TheraCal showed toxic effects after 24, 48, and 72 hr. Meanwhile, the highest cell migration was observed in the presence of CEM and Biodentine (P<0.05). The secretion of MCP-1 and TGF-β1 were higher in hDPSCs treated with Biodentine compared to some other groups (P<0.05, P<0.01). Moreover, TheraCal decreased protein secretion of TNF-α (P<0.05), and IL-8 (P<0.01) in hDPSCs. Conclusion: The biological compatibility associated with CEM and Biodentine indicates promising applications in the field of vital pulp therapy. [ABSTRACT FROM AUTHOR]

Aim: To clinically and radiographically evaluate the reparative dentin formation in indirect pulp treatment (IPT) using mineral trioxide aggregate (MTA) and light cured calcium silicate (TheraCal) in primary molars over a period of 6 months. Materials and Methods: A clinical trial on IPT on 43 primary molars in 21 patients between the age of 4–7 years, divided into two groups: 22 teeth in MTA group and 21 in TheraCal group. Measurement of the variation in dentin thickness was done on the digitalized radiograph at baseline, 3 months and 6 months using CorelDRAW X3 software. Results: Statistical analysis using an independent t-test for intragroup and intergroup comparison showed a significant increase in dentin thickness in both the MTA and TheraCal group (intragroup comparison [P < 0.05]). However, intergroup comparison between MTA and TheraCal showed no statistical difference in reparative dentin formation (P > 0.05). Conclusion: Clinically and radiographically, both MTA and TheraCal are good IPT materials. The better handling characteristics and comparable reparative dentin-forming ability of TheraCal make this material an alternative to MTA in pediatric restorative procedures.

Aim: To clinically and radiographically evaluate the reparative dentin formation in indirect pulp treatment (IPT) using mineral trioxide aggregate (MTA) and light cured calcium silicate (TheraCal) in primary molars over a period of 6 months. Materials and Methods: A clinical trial on IPT on 43 primary molars in 21 patients between the age of 4-7 years, divided into two groups: 22 teeth in MTA group and 21 in TheraCal group. Measurement of the variation in dentin thickness was done on the digitalized radiograph at baseline, 3 months and 6 months using CorelDRAW X3 software. Results: Statistical analysis using an independent t-test for intragroup and intergroup comparison showed a significant increase in dentin thickness in both the MTA and TheraCal group (intragroup comparison [P < 0.05]). However, intergroup comparison between MTA and TheraCal showed no statistical difference in reparative dentin formation (P > 0.05). Conclusion: Clinically and radiographically, both MTA and TheraCal are good IPT materials. The better handling characteristics and comparable reparative dentin-forming ability of TheraCal make this material an alternative to MTA in pediatric restorative procedures. [ABSTRACT FROM AUTHOR]