Abstract: To confirm the origin of the exchange coupling through the nano-oxide layer (NOL), the detailed analyses of the magnetization curve and the temperature dependence on magnetization for the Co1-xFex-NOL samples with various oxidation processes are investigated. The field cooling effect is observed for NOL-inserted samples, which suggests the existence of the antiferromagnetic (AFM) component in the NOL. The characteristic temperature (blocking temperature) increases with increase in the Fe content for Co1-xFex(x=0.08,0.17,0.26)-NOL. These results support that NOL pinning appears higher than room temperature. Further, the twisted coupling through the NOL observed for the Co0.50Fe0.50-NOL is discussed from the viewpoint of the magnetic roughness due to the ferrimagnetic nature of the very thin NOL in specular spin valve (SPSV). [Copyright &y& Elsevier]

Abstract: The Ni nano constriction dots embedded in the Ta-nano-oxide layer (NOL) was prepared by the ion beam sputtering (IBS) method. After the various conditions of the oxidations, the structural analyses of the NOL were performed by RHEED, AES and in situ STM/AFM observations. From the current image of the conductive AFM for NOL, the periodically aligned metallic dots with the size around 5–10nm were successfully observed. The mechanism of the formation of the self-organized aligned Ni nano constriction dots is discussed from the standpoint of the grain size, the crystal orientation, the preferred oxidation of Ta at the diffused interface. [Copyright &y& Elsevier]