Abstract: Graphene oxide (GO) dispersed polysulfone (PSf) mixed matrix membranes were prepared by wet phase inversion method. The morphology of membranes was studied using scanning electron microscope (SEM) images. The variation in hydrophilicity was studied by measuring surface wettability and water swelling experiments. The performance of membranes in terms of pure water flux and salt rejection was studied. SEM images depict enhanced macrovoids, while the contact angle data reveals that, GO incorporated membrane surface is moderately hydrophilic. Membranes exhibited improved salt rejection after GO doping. Membrane with 2000ppm GO loading has exhibited maximum of 72% Na2SO4 rejection at 4bar applied pressure. The salt rejection seems to depend on pH of the feed solution and it has been witnessed that the salt rejection showed an increasing trend with increase in the pH. [Copyright &y& Elsevier]

Abstract: Recently nanofiltration (NF) is gaining more importance for water treatment. It is replacing the conventional method of water treatment due to advantages of NF membranes over RO system. In this work, we are discussing the preparation of NF membrane for desalination of sea water. We herein report the synthesis of polymer, by the reaction of p-amino benzoic acid (PABA) and poly isobutylene-alt-maleic anhydride (PIAM) and its blend membrane preparation with polysulfone (PSf). The new membranes were characterized by SEM images, surface wettability to investigate the hydrophilic nature of the membrane, water swelling, pure water flux, molecular weight cut-off and salt rejection of the membranes. The membranes showed nano size (<50nm) pores in SEM image, and the contact angle data revealed that membrane surface is moderately hydrophilic. Membrane with 70:30 (PSf:modified PIAM) composition has shown good salt rejection of 96% at 200kPa for 3500ppm of NaCl solution with a pure water flux of 38.36Lm−2 h−1. [Copyright &y& Elsevier]