Highly ordered titania nanotubes (TNTs) were synthesised by an electrochemical anodization method for supercapacitor applications. However, the capacitive performance of the TNTs was relatively low and comparable to the conventional capacitor. Therefore, in order to improve the capacitive performance of the TNTs, a fast and facile electrochemical reduction method was applied to modify the TNTs (R-TNTs) by introducing oxygen vacancies into the lattice. X-ray photoelectron spectroscopy (XPS) data confirmed the presence of oxygen vacancies in the R-TNTs lattice upon the reduction of Ti4+ to Ti3+. Electrochemical reduction parameters such as applied voltage and reduction time were varied to optimize the best conditions for the modification process. The electrochemical performance of the samples was analyzed in a three-electrode configuration cell. The cyclic voltammogram recorded at 200 mV s−1 showed a perfect square-shaped voltammogram indicating the excellent electrochemical performance of R-TNTs prepared at 5 V for 30 s. The total area of the R-TNTs voltammogram was 3 times larger than the unmodified TNTs. A specific capacitance of 11.12 mF cm−2 at a current density of 20 μA cm−2 was obtained from constant current charge-discharge measurements, which was approximately 57 times higher than that of unmodified TNTs. R-TNTs also displayed outstanding cycle stability with 99% capacity retention after 1000 cycles. [ABSTRACT FROM AUTHOR]

Co-precipitation method was adopted in the preparation of nickel-cobalt oxides for potential application in supercapacitors. The formation of spinel nickel-cobalt oxide, NiCo2O4 started below 400 °C as confirmed by X-ray diffraction analysis. Pure phase nickel cobaltite with cation ratio of 1:2 (Ni:Co) was obtained at calcination temperature of 400 °C. The spinel phase decomposed gradually until 700 °C. The calcination time for the formation of NiCo2O4 was found to be between 2 to 4 h. The particle size of the prepared sample studied by transmission electron microscopy showed a value of 9.47 nm. The electrochemical properties of the metal oxide were measured in various acidic, neutral and alkaline electrolyte systems (1.0 M HCl, 1.0 M KCl and 1.0 M KOH) by employment of cyclic voltammetry, galvanostatic charge-discharge test and electrochemical impedance spectroscopy. Ideal capacitor behaviour with the largest operating voltage of 1.0 V and good electrochemical stability were observed in NiCo2O4 using neutral KCl aqueous electrolyte. Meanwhile, the prepared sample displayed the highest surface redox activity in 1.0 M KOH alkaline electrolyte but showed the lowest electrochemical performance in acidic electrolyte. At the current density of 0.5 A g−1, 1.0 M HCl, 1.0 M KCl and 1.0 M KOH gave specific capacitance values of 3.8, 41.9 and 249.8 F g−1 respectively. Copyright © 2015 John Wiley & Sons, Ltd. [ABSTRACT FROM AUTHOR]