A relatively simple, and high-efficiency method is reported to synthesize AlN nanowires, using catalyst-assisted chemical vapor deposition. A thin film of 5 nm Ni layer was deposited on sapphire as catalyst. Structural property of as-grown nanowires was investigated in detail by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) These large scale, high quality and uniform nanowires have smooth surface with diameter of 50 nm and length of 10–30 μ m, which are hexagonal single-crystalline with c = 0.497 nm, a = 0.272 nm and grow along [100] direction. Our results provide the first direct evidence of vapor-liquid-solid growth mechanism for AlN nanowires.

We have investigated growth conditions and structure of Wurzite AlN nanowires grown on sapphire (0002) substrates by chemical vapor deposition. The morphology, and structure were characterized by scanning electron microscopy, X-ray diffraction, and Raman analysis. Luminescence properties of AlN nanowires were studied by electron and photon excitation measurements, such as cathodoluminescence and photoluminescence. Band to band excitonic feature at 6.12 eV was first observed at room temperature in this study. Two typical defect band related transmissions around 3.0 eV and 4.85 eV were also observed, which are due to the radioactive recombination processes involving oxygen impurity and Al vacancies.

We have investigated the luminescence properties of single-chrystalline Wurtzite AlN nanowires by electron and photon excitation measurements, such as cathodoluminescence and photoluminescence. Band to band excitonic feature at 6.12eV was first observed at room temperature in this study. Two typical defect band related transmissions around 3.0eV and 4.85eV were also observed, which are due to the radioactive recombination processes involving oxygen impurity and Al vacancies. The Wurzite AlN nanowires were grown on sapphire (0002) substrates by catalyst-assisted chemical vapor deposition. The morphology and structure were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and Raman analysis.

We report a simple synthesis of AlN nanowires via catalyst-assisted chemical vapor deposition method. These high quality and uniform nanowires have smooth surface with diameter of 50 nm and length of 10–30 µ m, which are hexagonal single-crystal with lattice parameters c = 0.497 nm, a = 0.272 nm and grow along [100] direction. The morphology and structure were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and Raman analysis. Our results provide the first direct evidence of vapor-liquid-solid growth mechanism for the synthesis of AlN nanowires.